Preparation And Characterization Of Novel Iron (III) HydroxidePaper Mill Sludge Composite Adsorbent For Chromium Removal

Ali YARAŞ; Hasan ARSLANOĞLU

doi:https://doi.org/10.16984/saufenbilder.469464

Makale detayları

Preparation And Characterization Of Novel Iron (III) HydroxidePaper Mill Sludge Composite Adsorbent For Chromium Removal

Yazarlar:

Ali YARAŞ | Hasan ARSLANOĞLU

Ana Başlıklar:

Kimya mühendisliği

Dergi:

Sakarya University Journal of Science 2019 Vol.23 Issue 6, pp.1019-1026

Belge Tipi:

Makale

Yayın Tarihi:

11/2019

Belge Dili:

İngilizce

Document ID (Org No.):

2000556953

DOI:

https://doi.org/10.16984/saufenbilder.469464

Özet:

 


This work deals with
the removal of Cr (III) and Cr (VI) from synthetic solutions via a novel
composite adsorbent prepared by precipitating iron (III) hydroxide on paper
mill sludge (PMS). To obtain Fe(OH)3 loaded PMS, -8+16 mesh fraction
of PMS was saponified with NaOH solution, then iron (III) chloride was
impregnated, hydrolyzed in NaOH solution and dried. The influences of pH, time,
initial concentration and temperature on removal of Cr (III) and Cr (VI) were
examined and it was determined that Cr (VI) removal occurs simultaneously with
a reduction reaction. Maximum removal yields for Cr (III) and Cr (VI) occurred
at approximately pH = 5 and the adsorption achieved equilibrium in 90 min. Cr
(VI) adsorption ratio decreases while Cr (III) removal percentage increases
with raising in temperature. Experimental results are consistent with Langmuir
isotherm. Adsorption capacities of Cr (III) and Cr (VI) were calculated as
8.49, 10.14, 12.62 mg/g and 7.64, 5.39 and 4.17 mg/g for 25, 40 and 55 °C,
respectively. Enthalpy changes for Cr (III) and Cr (VI) were calculated as
24.67 kJ/mol and -12.46 kJ/mol, respectively. These results demonstrated that
the adsorption phenomenon of Cr (III) and Cr (VI) are endothermic and
exothermic.


.

Makale detayları

Preparation And Characterization Of Novel Iron (III) HydroxidePaper Mill Sludge Composite Adsorbent For Chromium Removal

Yazarlar: Ali YARAŞ | Hasan ARSLANOĞLU

Ana Başlıklar: Kimya mühendisliği

Dergi: Sakarya University Journal of Science 2019 Vol.23 Issue 6, pp.1019-1026

Belge Tipi: Makale

Yayın Tarihi: 11/2019

Belge Dili: İngilizce

Document ID (Org No.): 2000556953

DOI: https://doi.org/10.16984/saufenbilder.469464

Sayı

Yazarlar:

Ali YARAŞ | Hasan ARSLANOĞLU

Ana Başlıklar:

Kimya mühendisliği

Dergi:

Sakarya University Journal of Science 2019 Vol.23 Issue 6, pp.1019-1026

Belge Tipi:

Makale

Yayın Tarihi:

11/2019

Belge Dili:

İngilizce

Document ID (Org No.):

2000556953

DOI:

https://doi.org/10.16984/saufenbilder.469464