Experimental and Analytical Investigation of Moment-Carrying Capacities of Reinforced Concrete Frame Systems Corroded by Accelerated Corrosion Method

Ahmet İhsan Turan; Yaşar Ayaz; Hakan Yalçıner; Atila Kumbasaroğlu; Alper Çelik

Makale detayları

Experimental and Analytical Investigation of Moment-Carrying Capacities of Reinforced Concrete Frame Systems Corroded by Accelerated Corrosion Method

Yazarlar:

Ahmet İhsan Turan | Yaşar Ayaz | Hakan Yalçıner | Atila Kumbasaroğlu | Alper Çelik

Yayıncı:

Igdir University

Ana Başlıklar:

Betonarme Yapılar

Dergi:

Iğdır Üniversitesi Fen Bilimleri Enstitüsü Dergisi Vol.14 Issue 2, pp.755-772

Belge Tipi:

Makale

Yayın Tarihi:

1/2024

Belge Dili:

İngilizce

Document ID (Org No.):

2001317807

pISSN:

2536-4618

Anahtar kelimeler:

Özet:

 Technical investigations carried out after the devastating earthquakes in Turkey in the last 25 years show that one of the main causes of damage to reinforced concrete structures is reinforcement bar corrosion. The deterioration caused by reinforcement corrosion in reinforced concrete elements reduces the parameters that define the performance level of the structure, such as ductility, stiffness, bond-slip relationship, load carrying capacity, and energy absorption capacity. Therefore, determining the specified performance levels of reinforced concrete structures exposed to corrosion before any seismic activity occurs is of great importance in preventing loss of life and property. Cross-section behavior in reinforced concrete structures represents the load-bearing element behavior In order to accurately determine the section behavior, the Moment-Curvature relationship must be defined. In this study, the structural behavior of reinforced concrete frames exposed to corrosion was examined experimentally and analytically. For this purpose, 4 of the 5 reinforced concrete frame specimens constructed were corroded at different ratios using the accelerated corrosion method. After the corrosion process was completed, in the experimental part of the study, all specimens were tested under the effect of a 20 constant axial load and reversal-cyclic loading. In the analytical study, as a result of the cross-sectional analyzes carried out by taking into account the material-mechanical properties changing with the effect of corrosion, it was determined that the calculated moment values were in high predicted with the experimentally measured moment values.

 Technical investigations carried out after the devastating earthquakes in Turkey in the last 25 years show that one of the main causes of damage to reinforced concrete structures is reinforcement bar corrosion. The deterioration caused by reinforcement corrosion in reinforced concrete elements reduces the parameters that define the performance level of the structure, such as ductility, stiffness, bond-slip relationship, load carrying capacity, and energy absorption capacity. Therefore, determining the specified performance levels of reinforced concrete structures exposed to corrosion before any seismic activity occurs is of great importance in preventing loss of life and property. Cross-section behavior in reinforced concrete structures represents the load-bearing element behavior In order to accurately determine the section behavior, the Moment-Curvature relationship must be defined. In this study, the structural behavior of reinforced concrete frames exposed to corrosion was examined experimentally and analytically. For this purpose, 4 of the 5 reinforced concrete frame specimens constructed were corroded at different ratios using the accelerated corrosion method. After the corrosion process was completed, in the experimental part of the study, all specimens were tested under the effect of a 20 constant axial load and reversal-cyclic loading. In the analytical study, as a result of the cross-sectional analyzes carried out by taking into account the material-mechanical properties changing with the effect of corrosion, it was determined that the calculated moment values were in high predicted with the experimentally measured moment values.

 Technical investigations carried out after the devastating earthquakes in Turkey in the last 25 years show that one of the main causes of damage to reinforced concrete structures is reinforcement bar corrosion. The deterioration caused by reinforcement corrosion in reinforced concrete elements reduces the parameters that define the performance level of the structure, such as ductility, stiffness, bond-slip relationship, load carrying capacity, and energy absorption capacity. Therefore, determining the specified performance levels of reinforced concrete structures exposed to corrosion before any seismic activity occurs is of great importance in preventing loss of life and property. Cross-section behavior in reinforced concrete structures represents the load-bearing element behavior In order to accurately determine the section behavior, the Moment-Curvature relationship must be defined. In this study, the structural behavior of reinforced concrete frames exposed to corrosion was examined experimentally and analytically. For this purpose, 4 of the 5 reinforced concrete frame specimens constructed were corroded at different ratios using the accelerated corrosion method. After the corrosion process was completed, in the experimental part of the study, all specimens were tested under the effect of a 20 constant axial load and reversal-cyclic loading. In the analytical study, as a result of the cross-sectional analyzes carried out by taking into account the material-mechanical properties changing with the effect of corrosion, it was determined that the calculated moment values were in high predicted with the experimentally measured moment values.

 Türkiyede son 25 yılda yaşanan yıkıcı depremlerin ardından yapılan teknik incelemeler, betonarme yapılarda meydana gelen hasarların ana sebeplerinden birinin de donatı korozyonu olduğunu vurgulamaktadır. Donatı korozyonunun betonarme elemanlarda meydana getirdiği bozulmalar, yapının performans seviyesini tanımlayan süneklik, rijitlik, aderans-donatı sıyrılması ilişkisi, taşıma gücü ve enerji yutma kapasitesi gibi parametrelerin azalmasına sebep olmaktadır. Bu bağlamda olası bir sismik hareketlilik yaşanmadan korozyona maruz kalmış betonarme yapıların belirtilen bu performans seviyelerinin tespit edilmesi can ve mal kayıplarının önüne geçilmesi açısından büyük öneme sahiptir. Betonarme yapılarda taşıyıcı eleman davranışını, kesit davranışı yansıtmaktadır. Kesit davranışının doğru bir şekilde tespit edilebilmesi için de Moment-Eğrilik ilişkisinin tanımlanması gerekmektedir. Gerçekleştirilen çalışma ile birlikte korozyona maruz bırakılmış betonarme çerçevelerin yapısal davranışları deneysel ve analitik olarak incelenmiştir. Bu kapsamda üretilen 5 adet betonarme çerçeve numunesinden 4 adedi hızlandırılmış korozyon yöntemiyle farklı oranlarda paslandırılmıştır. Korozyon sürecinin tamamlanmasının ardından, çalışmanın deneysel bölümünde tüm numuneler 20 eksenel ve tersinir-tekrarlanır yanal yük altında deneye tabi tutulmuştur. Analitik çalışmada, korozyon etkisiyle değişen malzeme-mekanik özellikleri dikkate alınarak gerçekleştirilen kesit analizleri sonucunda, hesap edilen moment değerlerinin deneysel olarak ölçülen moment değerleriyle yüksek oranda uyum gösterdiği tespit edilmiştir.

Makale detayları

Experimental and Analytical Investigation of Moment-Carrying Capacities of Reinforced Concrete Frame Systems Corroded by Accelerated Corrosion Method

Yazarlar:

Ahmet İhsan Turan | Yaşar Ayaz | Hakan Yalçıner | Atila Kumbasaroğlu | Alper Çelik

Yayıncı:

Igdir University

Ana Başlıklar:

Betonarme Yapılar

Dergi:

Iğdır Üniversitesi Fen Bilimleri Enstitüsü Dergisi Vol.14 Issue 2, pp.755-772

Belge Tipi:

Makale

Yayın Tarihi:

1/2024

Belge Dili:

İngilizce

Document ID (Org No.):

2001317807

pISSN:

2536-4618

Corrosion

Section analysis

Rc frames

Cyclic load

Moment-curvature relationshipKorozyon

Kesit analizi

Betonarme çerçeve

Çevrimsel yükleme

Moment-eğrilik ilişkisi

Sayı

Makale detayları

Yazarlar: Ahmet İhsan Turan | Yaşar Ayaz | Hakan Yalçıner | Atila Kumbasaroğlu | Alper Çelik

Yayıncı: Igdir University

Ana Başlıklar: Betonarme Yapılar

Dergi: Iğdır Üniversitesi Fen Bilimleri Enstitüsü Dergisi Vol.14 Issue 2, pp.755-772

Belge Tipi: Makale

Yayın Tarihi: 1/2024

Belge Dili: İngilizce

Document ID (Org No.): 2001317807

pISSN: 2536-4618

Sayı

Yazarlar:

Ahmet İhsan Turan | Yaşar Ayaz | Hakan Yalçıner | Atila Kumbasaroğlu | Alper Çelik

Yayıncı:

Igdir University

Ana Başlıklar:

Betonarme Yapılar

Dergi:

Iğdır Üniversitesi Fen Bilimleri Enstitüsü Dergisi Vol.14 Issue 2, pp.755-772

Belge Tipi:

Makale

Yayın Tarihi:

1/2024

Belge Dili:

İngilizce

Document ID (Org No.):

2001317807

pISSN:

2536-4618