Structural and Magnetic Effects of Sb and Ag Co-Substitution on  (Bi, Pb) – 2223 Systems

Gönül Bilgeç Akyüz; Filiz Aksoy

Makale detayları

Structural and Magnetic Effects of Sb and Ag Co-Substitution on (Bi, Pb) – 2223 Systems

Yazarlar:

Gönül Bilgeç Akyüz | Filiz Aksoy

Yayıncı:

Afyon Kocatepe University

Ana Başlıklar:

Klasik Fizik (Diğer)

Dergi:

Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi Vol.25 Issue 2, pp.261-268

Belge Tipi:

Makale

Yayın Tarihi:

11/2025

Belge Dili:

Türkçe

Document ID (Org No.):

2001344396

pISSN:

2149-3367

Anahtar kelimeler:

Özet:

 In this study, structural and magnetic effects of partial displacements of lead-doped Bismuth-based High Temperature Superconductors Bi, Pb  2223 on the Pb and Cu region for some determined values of Sb and Ag, respectively, have been investigated. Sb-Ag doping has been done for five different values in the range of x0.00-0.20 in the high temperature superconducting composition in the form of Bi1.7Pb0.3-xSbxSr2Ca2Cu3-xAgxOy prepared by Solid-State Reaction method. By evaluating the XRD, SEM, EDAX and M-T analysis results of these materials; the effect of doping element Sb and Ag, the substituted region and the amount of substitution x on the superconducting structure have been investigated. In addition, using these analyzes, the lattice parameters of the materials, the type of cyrstal structures, the ratio of high and low temperature phases, particle sizes and effect on critical temperature have been determined. When the results are examined, it is observed that this displacement process have significant effects on critical temperatures, superconductivity phases of samples and the structure, connectivity and dimensions of the particles that composed of the material.

 In this study, structural and magnetic effects of partial displacements of lead-doped Bismuth-based High Temperature Superconductors Bi, Pb  2223 on the Pb and Cu region for some determined values of Sb and Ag, respectively, have been investigated. Sb-Ag doping has been done for five different values in the range of x0.00-0.20 in the high temperature superconducting composition in the form of Bi1.7Pb0.3-xSbxSr2Ca2Cu3-xAgxOy prepared by Solid-State Reaction method. By evaluating the XRD, SEM, EDAX and M-T analysis results of these materials; the effect of doping element Sb and Ag, the substituted region and the amount of substitution x on the superconducting structure have been investigated. In addition, using these analyzes, the lattice parameters of the materials, the type of cyrstal structures, the ratio of high and low temperature phases, particle sizes and effect on critical temperature have been determined. When the results are examined, it is observed that this displacement process have significant effects on critical temperatures, superconductivity phases of samples and the structure, connectivity and dimensions of the particles that composed of the material.

 In this study, structural and magnetic effects of partial displacements of lead-doped Bismuth-based High Temperature Superconductors Bi, Pb  2223 on the Pb and Cu region for some determined values of Sb and Ag, respectively, have been investigated. Sb-Ag doping has been done for five different values in the range of x0.00-0.20 in the high temperature superconducting composition in the form of Bi1.7Pb0.3-xSbxSr2Ca2Cu3-xAgxOy prepared by Solid-State Reaction method. By evaluating the XRD, SEM, EDAX and M-T analysis results of these materials; the effect of doping element Sb and Ag, the substituted region and the amount of substitution x on the superconducting structure have been investigated. In addition, using these analyzes, the lattice parameters of the materials, the type of cyrstal structures, the ratio of high and low temperature phases, particle sizes and effect on critical temperature have been determined. When the results are examined, it is observed that this displacement process have significant effects on critical temperatures, superconductivity phases of samples and the structure, connectivity and dimensions of the particles that composed of the material.

 Bu çalışmada, kurşun katkılı Bizmut-tabanlı Yüksek Sıcaklık Süperiletkenlerin Bi, Pb  2223 Pb bölgesine Sb ve Cu bölgesine Agnin belirlenen bazı değerleri için yapılan kısmi yer değiştirmelerin yapısal ve manyetik etkileri araştırılmıştır. Katı-Hal Reaksiyon yöntemi ile hazırlanan Bi1.7Pb0.3-xSbxSr2Ca2Cu3-xAgxOy formundaki yüksek sıcaklık süperiletken bileşiminde, Sb-Ag katkılamaları x0.00-0.20 aralığındaki beş farklı değer için yapılmıştır. Bu malzemelerin, XRD, SEM, EDAX ve M-T analiz sonuçları değerlendirilerek; katkılanan Sb ve Ag elementlerinin, süperiletken malzeme içinde yer değiştirme işleminin yapıldığı bölgenin ve yer değiştirme miktarlarının x, süperiletken yapıya etkisi incelenmiştir. Ayrıca bu analizler kullanılarak, malzemelerin örgü parametreleri, kristal yapılarının çeşidi, yüksek ve düşük sıcaklık fazlarının oranı, tanecik boyutları ve kritik sıcaklığa etkisi belirlenmiştir. Sonuçlar incelendiğinde, yapılan bu yer değiştirme işleminin, numunelerin kritik sıcaklıkları, süperiletkenlik fazları, malzemeyi oluşturan taneciklerin yapısı, bağlanabilirliği ve boyutları üzerinde önemli etkiler oluşturduğu gözlenmiştir.

Makale detayları

Structural and Magnetic Effects of Sb and Ag Co-Substitution on (Bi, Pb) – 2223 Systems

Yazarlar:

Gönül Bilgeç Akyüz | Filiz Aksoy

Yayıncı:

Afyon Kocatepe University

Ana Başlıklar:

Klasik Fizik (Diğer)

Dergi:

Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi Vol.25 Issue 2, pp.261-268

Belge Tipi:

Makale

Yayın Tarihi:

11/2025

Belge Dili:

Türkçe

Document ID (Org No.):

2001344396

pISSN:

2149-3367

Effect of Sb-Ag Co-Substitution

SEM

XRD

M-T

(Bi,Pb)-2223Sb-Ag Etkisi

SEM

XRD

M-T

Sayı

Makale detayları

Yazarlar: Gönül Bilgeç Akyüz | Filiz Aksoy

Yayıncı: Afyon Kocatepe University

Ana Başlıklar: Klasik Fizik (Diğer)

Dergi: Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi Vol.25 Issue 2, pp.261-268

Belge Tipi: Makale

Yayın Tarihi: 11/2025

Belge Dili: Türkçe

Document ID (Org No.): 2001344396

pISSN: 2149-3367

Sayı

Yazarlar:

Gönül Bilgeç Akyüz | Filiz Aksoy

Yayıncı:

Afyon Kocatepe University

Ana Başlıklar:

Klasik Fizik (Diğer)

Dergi:

Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi Vol.25 Issue 2, pp.261-268

Belge Tipi:

Makale

Yayın Tarihi:

11/2025

Belge Dili:

Türkçe

Document ID (Org No.):

2001344396

pISSN:

2149-3367