Study on Strength Properties of of Woven Fabrics Including Recycled Cotton Yarns.

Mihriban Kalkancı

Makale detayları

Study on Strength Properties of of Woven Fabrics Including Recycled Cotton Yarns.

Yazarlar:

Mihriban Kalkancı

Yayıncı:

Bitlis Eren University

Ana Başlıklar:

Fabric Technologies | Textile Technology

Dergi:

Bitlis Eren Üniversitesi Fen Bilimleri Dergisi Vol.13 Issue 3, pp.779-787

Belge Tipi:

Makale

Yayın Tarihi:

9/2024

Belge Dili:

İngilizce

Document ID (Org No.):

2001327661

pISSN:

2147-3129

Anahtar kelimeler:

Özet:

 In this study, plain fabrics were produced from yarns obtained from cotton fibers and recycled cotton fibers obtained from yarn waste. Within the scope of the study, yarns with cottonrecycled cotton fiber ratios of 100-0, 90-10, 80-20, 70-30, 60-40 were used. All fabrics were subjected to finishing processes respectively under the same conditions. Breaking strength and tear strength tests were carried out to understand the effect of the recycling rate on the strength loss in fabrics. In the research, important findings were reached regarding these fabrics. It was determined that there was a decrease of nearly 45 in the tear strength of fabrics obtained by mixing 40 recycled fiber. Additionally, the loss in tensile strength was less than the loss in tear strength.

 In this study, plain fabrics were produced from yarns obtained from cotton fibers and recycled cotton fibers obtained from yarn waste. Within the scope of the study, yarns with cottonrecycled cotton fiber ratios of 100-0, 90-10, 80-20, 70-30, 60-40 were used. All fabrics were subjected to finishing processes respectively under the same conditions. Breaking strength and tear strength tests were carried out to understand the effect of the recycling rate on the strength loss in fabrics. In the research, important findings were reached regarding these fabrics. It was determined that there was a decrease of nearly 45 in the tear strength of fabrics obtained by mixing 40 recycled fiber. Additionally, the loss in tensile strength was less than the loss in tear strength.

 In this study, plain fabrics were produced from yarns obtained from cotton fibers and recycled cotton fibers obtained from yarn waste. Within the scope of the study, yarns with cottonrecycled cotton fiber ratios of 100-0, 90-10, 80-20, 70-30, 60-40 were used. All fabrics were subjected to finishing processes respectively under the same conditions. Breaking strength and tear strength tests were carried out to understand the effect of the recycling rate on the strength loss in fabrics. In the research, important findings were reached regarding these fabrics. It was determined that there was a decrease of nearly 45 in the tear strength of fabrics obtained by mixing 40 recycled fiber. Additionally, the loss in tensile strength was less than the loss in tear strength.

 In this study, plain fabrics were produced from yarns obtained from cotton fibers and recycled cotton fibers obtained from yarn waste. Within the scope of the study, yarns with cottonrecycled cotton fiber ratios of 100-0, 90-10, 80-20, 70-30, 60-40 were used. All fabrics were subjected to finishing processes respectively under the same conditions. Breaking strength and tear strength tests were carried out to understand the effect of the recycling rate on the strength loss in fabrics. In the research, important findings were reached regarding these fabrics. It was determined that there was a decrease of nearly 45 in the tear strength of fabrics obtained by mixing 40 recycled fiber. Additionally, the loss in tensile strength was less than the loss in tear strength.

Makale detayları

Study on Strength Properties of of Woven Fabrics Including Recycled Cotton Yarns.

Yazarlar:

Mihriban Kalkancı

Yayıncı:

Bitlis Eren University

Ana Başlıklar:

Fabric Technologies | Textile Technology

Dergi:

Bitlis Eren Üniversitesi Fen Bilimleri Dergisi Vol.13 Issue 3, pp.779-787

Belge Tipi:

Makale

Yayın Tarihi:

9/2024

Belge Dili:

İngilizce

Document ID (Org No.):

2001327661

pISSN:

2147-3129

Recycled cotton fabric

Strength properties

Recycling

Recycled woven fabric

Fabric properties

Sayı

Makale detayları

Study on Strength Properties of of Woven Fabrics Including Recycled Cotton Yarns.

Yazarlar: Mihriban Kalkancı

Yayıncı: Bitlis Eren University

Ana Başlıklar: Fabric Technologies | Textile Technology

Dergi: Bitlis Eren Üniversitesi Fen Bilimleri Dergisi Vol.13 Issue 3, pp.779-787

Belge Tipi: Makale

Yayın Tarihi: 9/2024

Belge Dili: İngilizce

Document ID (Org No.): 2001327661

pISSN: 2147-3129

Recycled cotton fabric

Strength properties

Recycling

Recycled woven fabric

Fabric properties

Sayı

Yazarlar:

Mihriban Kalkancı

Yayıncı:

Bitlis Eren University

Ana Başlıklar:

Fabric Technologies | Textile Technology

Dergi:

Bitlis Eren Üniversitesi Fen Bilimleri Dergisi Vol.13 Issue 3, pp.779-787

Belge Tipi:

Makale

Yayın Tarihi:

9/2024

Belge Dili:

İngilizce

Document ID (Org No.):

2001327661

pISSN:

2147-3129