CO2 Capture Analysis of Tobacco Biochar-AlCl3 Composite

Nejmi SOYLER; Selim CEYLAN; Yildiray TOPCU

Makale detayları

CO2 Capture Analysis of Tobacco Biochar-AlCl3 Composite

Yazarlar:

Nejmi SOYLER | Selim CEYLAN | Yildiray TOPCU

Yayıncı:

Yildiz Technical University

Ana Başlıklar:

Kanalizasyon ve beledi mühendislik

Dergi:

Environmental Research and Technology 2018 Vol.1 Issue 1, pp.34-37

Belge Tipi:

Makale

Yayın Tarihi:

12/2017

Belge Dili:

Türkçe

Document ID (Org No.):

2000409552

eISSN:

2636-8498

Özet:

 


In
this study, the performance of tobacco biochar-AlCl3 composite for
CO2 capture was investigated. Biochar-AlCl3 composites
were prepared at different blend ratios (10:0.4; 10:2; 10:4, wt./wt.) and used
for CO2 capture experiments to determine the optimal Al metal
content at which CO2 adsorption was highest. Biochar composites were
produced through slow pyrolysis under inert nitrogen atmosphere in a fixed bed
reactor at 600oC for 3h. Properties of biochar-metal composites and
raw biochar samples were characterized with SEM-EDS, XRD and FTIR analysis. CO2
experiments were conducted in TGA under N2 atmosphere with a flow
rate of 50 ml/min at 25°C. The maximum CO2 adsorption was observed as 59.97
mg/g for biochar: AlCl3 composite at a ratio of 10:2. Finally,
results of study showed that biochar-AlCl3 composites have great
potential as a CO2 capture material due to its low-cost,
sustainability and CO2 capture capacity.


.

Makale detayları

CO2 Capture Analysis of Tobacco Biochar-AlCl3 Composite

Yazarlar: Nejmi SOYLER | Selim CEYLAN | Yildiray TOPCU

Yayıncı: Yildiz Technical University

Ana Başlıklar: Kanalizasyon ve beledi mühendislik

Dergi: Environmental Research and Technology 2018 Vol.1 Issue 1, pp.34-37

Belge Tipi: Makale

Yayın Tarihi: 12/2017

Belge Dili: Türkçe

Document ID (Org No.): 2000409552

eISSN: 2636-8498

Sayı

Yazarlar:

Nejmi SOYLER | Selim CEYLAN | Yildiray TOPCU

Yayıncı:

Yildiz Technical University

Ana Başlıklar:

Kanalizasyon ve beledi mühendislik

Dergi:

Environmental Research and Technology 2018 Vol.1 Issue 1, pp.34-37

Belge Tipi:

Makale

Yayın Tarihi:

12/2017

Belge Dili:

Türkçe

Document ID (Org No.):

2000409552

eISSN:

2636-8498