Molten Salt Approach for Co3O4 Synthesis as a Charge Storage Electrode

Ümran Kurtan

Makale detayları

Molten Salt Approach for Co3O4 Synthesis as a Charge Storage Electrode

Yazarlar:

Ümran Kurtan

Yayıncı:

Afyon Kocatepe University

Ana Başlıklar:

Kimya Mühendisliği

Dergi:

Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi Vol.23 Issue 5, pp.1256-1266

Belge Tipi:

Makale

Yayın Tarihi:

10/2023

Belge Dili:

İngilizce

Document ID (Org No.):

2001302514

pISSN:

2149-3367

Anahtar kelimeler:

Özet:

 A versatile molten salt method was targeted to fabricate the cobalt oxide Co3O4 nanospheres as charge storage electrodes. The Co3O4 nanospheres were prepared in KNO3 molten salt in only one step within 5 minutes. The nanospheres were with an average size distribution of almost 80-130 nm. The specific capacitance of cobalt oxide was found to be 285 Fg at 10 mVs and 171 Fg at 0.5 A g in 6 M KOH and the Trasatti method was used to understand the outer and inner surface capacitive contributions. The material possessed a moderate rate capability 63.1 at 5 Ag and had good cyclic stability 90.5 after 1200 cycles. This experimental study does not require any solvent usage and thus can provide a green and continuous approach for the preparation of various transition metal oxides with good electrochemical properties in the energy storage field.

 A versatile molten salt method was targeted to fabricate the cobalt oxide Co3O4 nanospheres as charge storage electrodes. The Co3O4 nanospheres were prepared in KNO3 molten salt in only one step within 5 minutes. The nanospheres were with an average size distribution of almost 80-130 nm. The specific capacitance of cobalt oxide was found to be 285 Fg at 10 mVs and 171 Fg at 0.5 A g in 6 M KOH and the Trasatti method was used to understand the outer and inner surface capacitive contributions. The material possessed a moderate rate capability 63.1 at 5 Ag and had good cyclic stability 90.5 after 1200 cycles. This experimental study does not require any solvent usage and thus can provide a green and continuous approach for the preparation of various transition metal oxides with good electrochemical properties in the energy storage field.

 A versatile molten salt method was targeted to fabricate the cobalt oxide Co3O4 nanospheres as charge storage electrodes. The Co3O4 nanospheres were prepared in KNO3 molten salt in only one step within 5 minutes. The nanospheres were with an average size distribution of almost 80-130 nm. The specific capacitance of cobalt oxide was found to be 285 Fg at 10 mVs and 171 Fg at 0.5 A g in 6 M KOH and the Trasatti method was used to understand the outer and inner surface capacitive contributions. The material possessed a moderate rate capability 63.1 at 5 Ag and had good cyclic stability 90.5 after 1200 cycles. This experimental study does not require any solvent usage and thus can provide a green and continuous approach for the preparation of various transition metal oxides with good electrochemical properties in the energy storage field.

 Yük depolama elektrotları olarak kobalt oksit Co3O4 nanokürelerini sentezlemek için çok yönlü bir eriyik tuz yöntemi hedeflenmiştir. Co3O4 nanoküreleri KNO3 erimiş tuzunda sadece tek adımda 5 dakika içerisinde hazırlanmıştır. Nanokürelerin ortalama boyut dağılımı yaklaşık 80-130 nmdir. Kobalt oksidin spesifik kapasitansı 6 M KOH elektrolitinde 10 mVsde 285 Fg ve 0.5 Agda 171 Fg olarak bulunmuş ve dış ve iç yüzey kapasitif katkılarını anlamak için Trasatti yöntemi kullanılmıştır. Malzeme orta seviyede bir kapasite koruması 5 Agda 63.1 ve iyi bir döngüsel kararlılık 1200 çevrim sonrası 90.5 göstermiştir. Bu deneysel çalışma herhangi bir çözücü kullanımını gerektirmemektedir ve bu nedenle enerji depolama alanında iyi elektrokimyasal özelliklere sahip çeşitli geçiş metal oksitlerinin hazırlanması için yeşil ve sürekli bir yaklaşım sağlayabilir.

Makale detayları

Molten Salt Approach for Co3O4 Synthesis as a Charge Storage Electrode

Yazarlar:

Ümran Kurtan

Yayıncı:

Afyon Kocatepe University

Ana Başlıklar:

Kimya Mühendisliği

Dergi:

Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi Vol.23 Issue 5, pp.1256-1266

Belge Tipi:

Makale

Yayın Tarihi:

10/2023

Belge Dili:

İngilizce

Document ID (Org No.):

2001302514

pISSN:

2149-3367

Molten Salt Method

Cobalt Oxide

Electrode

Energy StorageEriyik Tuz Yöntemi

Kobalt Oksit

Elektrot

Enerji Depolama

Sayı

Makale detayları

Yazarlar: Ümran Kurtan

Yayıncı: Afyon Kocatepe University

Ana Başlıklar: Kimya Mühendisliği

Dergi: Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi Vol.23 Issue 5, pp.1256-1266

Belge Tipi: Makale

Yayın Tarihi: 10/2023

Belge Dili: İngilizce

Document ID (Org No.): 2001302514

pISSN: 2149-3367

Sayı

Yazarlar:

Ümran Kurtan

Yayıncı:

Afyon Kocatepe University

Ana Başlıklar:

Kimya Mühendisliği

Dergi:

Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi Vol.23 Issue 5, pp.1256-1266

Belge Tipi:

Makale

Yayın Tarihi:

10/2023

Belge Dili:

İngilizce

Document ID (Org No.):

2001302514

pISSN:

2149-3367