Ti6Al4V Alaşımı ve Saf Titanyumun (Cp-Ti) Oksidasyon Kinetiği

Aysun AYDAY

Makale detayları

Ti6Al4V Alaşımı ve Saf Titanyumun (Cp-Ti) Oksidasyon Kinetiği

Yazarlar:

Aysun AYDAY

Yayıncı:

Tayfun UYGUNOĞLU

Ana Başlıklar:

Uygulamalı fizik

Dergi:

El-Cezeri 2020 Vol.7 Issue 2, pp.402-409

Belge Tipi:

Makale

Yayın Tarihi:

5/2020

Belge Dili:

Türkçe

Document ID (Org No.):

2000406833

eISSN:

2148-3736

pISSN:

2148-3736

Özet:

 


The oxidation kinetics behavior of Ti6Al4V alloy and pure Ti (Cp-Ti) were investigated under air atmosphere at temperatures of 600, 650 and 700 °C for 1, 2, 4, 8, 16, 24, 48, 72 h have been identified in the study. The oxidized samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM). After thermal oxidation, a thin oxide layer was formed on the surfaces and oxygen diffusion took place into the metal. The oxide layer formed rutile and anatase (TiO2) form. The thickness of the oxide layer increased with increasing the oxidation temperature and time The activation energies for oxidation were estimated for Ti6Al4V alloys and Cp-Ti, 201.3kJ/mol for Ti6Al4V and 269.4kJ/mol for Cp-Ti were found, respectively. 

.

Makale detayları

Ti6Al4V Alaşımı ve Saf Titanyumun (Cp-Ti) Oksidasyon Kinetiği

Yazarlar: Aysun AYDAY

Yayıncı: Tayfun UYGUNOĞLU

Ana Başlıklar: Uygulamalı fizik

Dergi: El-Cezeri 2020 Vol.7 Issue 2, pp.402-409

Belge Tipi: Makale

Yayın Tarihi: 5/2020

Belge Dili: Türkçe

Document ID (Org No.): 2000406833

eISSN: 2148-3736

pISSN: 2148-3736

Sayı

Yazarlar:

Aysun AYDAY

Yayıncı:

Tayfun UYGUNOĞLU

Ana Başlıklar:

Uygulamalı fizik

Dergi:

El-Cezeri 2020 Vol.7 Issue 2, pp.402-409

Belge Tipi:

Makale

Yayın Tarihi:

5/2020

Belge Dili:

Türkçe

Document ID (Org No.):

2000406833

eISSN:

2148-3736

pISSN:

2148-3736