The influence of microwave curing on the strength of silica fume-added fly ash-based geopolymer mortars

Berivan Yılmazer Polat

Makale detayları

The influence of microwave curing on the strength of silica fume-added fly ash-based geopolymer mortars

Yazarlar:

Berivan Yılmazer Polat

Yayıncı:

Yildiz Technical University

Ana Başlıklar:

Materials Engineering (Other)

Dergi:

Journal of Sustainable Construction Materials and Technologies Vol.8 Issue 3, pp.207-215

Belge Tipi:

Makale

Yayın Tarihi:

3/2023

Belge Dili:

İngilizce

Document ID (Org No.):

2001299824

pISSN:

2458-973X

Anahtar kelimeler:

Özet:

 Geopolymer concretes a substitute for traditional Portland cement as a more environmentally sustainable alternative. In addition, one of the most significant advantages of geopolymer concrete is the high setting speed that can be achieved with thermal curing, that is, the short curing period. Research on geopolymer concrete has focused on curing, where curing is usually done with conventional ovens. Microwave curing initiates heat generation at the molecular level, which results in a minimal heat increase on the surface of the specimens compared to traditional thermal curing methods. In addition, it provides internal, rapid, and homogeneous heating and rapid strength development. This study is based on research that examined the effect of microwave cure on the compressive strength of silica füme-modified geopolymer mortar. In the study, sodium silicate and sodium hydroxide were used for activation, and first of all, fly ash substituted geopolymer mortar specimens were subjected to conventional thermal curing in an oven. On the other hand, the mortar specimens with the same composition were subjected to short-duration 10 minutes microwave curing at power levels of between 200-600 W. When the results were compared regarding compressive strength, void and percent water absorption, UPV, and SEM-internal structure examination, it was revealed that microwave curing could be used faster than the conventional oven curing method in silica füme-added fly ash-based geopolymer mortars. This research can be considered an essential step for further optimizing and popularising geopolymer concrete and microwave curing and proposes a method that should be considered in the future development of more sustainable construction materials.

 Geopolymer concretes a substitute for traditional Portland cement as a more environmentally sustainable alternative. In addition, one of the most significant advantages of geopolymer concrete is the high setting speed that can be achieved with thermal curing, that is, the short curing period. Research on geopolymer concrete has focused on curing, where curing is usually done with conventional ovens. Microwave curing initiates heat generation at the molecular level, which results in a minimal heat increase on the surface of the specimens compared to traditional thermal curing methods. In addition, it provides internal, rapid, and homogeneous heating and rapid strength development. This study is based on research that examined the effect of microwave cure on the compressive strength of silica füme-modified geopolymer mortar. In the study, sodium silicate and sodium hydroxide were used for activation, and first of all, fly ash substituted geopolymer mortar specimens were subjected to conventional thermal curing in an oven. On the other hand, the mortar specimens with the same composition were subjected to short-duration 10 minutes microwave curing at power levels of between 200-600 W. When the results were compared regarding compressive strength, void and percent water absorption, UPV, and SEM-internal structure examination, it was revealed that microwave curing could be used faster than the conventional oven curing method in silica füme-added fly ash-based geopolymer mortars. This research can be considered an essential step for further optimizing and popularising geopolymer concrete and microwave curing and proposes a method that should be considered in the future development of more sustainable construction materials.

 Geopolymer concretes a substitute for traditional Portland cement as a more environmentally sustainable alternative. In addition, one of the most significant advantages of geopolymer concrete is the high setting speed that can be achieved with thermal curing, that is, the short curing period. Research on geopolymer concrete has focused on curing, where curing is usually done with conventional ovens. Microwave curing initiates heat generation at the molecular level, which results in a minimal heat increase on the surface of the specimens compared to traditional thermal curing methods. In addition, it provides internal, rapid, and homogeneous heating and rapid strength development. This study is based on research that examined the effect of microwave cure on the compressive strength of silica füme-modified geopolymer mortar. In the study, sodium silicate and sodium hydroxide were used for activation, and first of all, fly ash substituted geopolymer mortar specimens were subjected to conventional thermal curing in an oven. On the other hand, the mortar specimens with the same composition were subjected to short-duration 10 minutes microwave curing at power levels of between 200-600 W. When the results were compared regarding compressive strength, void and percent water absorption, UPV, and SEM-internal structure examination, it was revealed that microwave curing could be used faster than the conventional oven curing method in silica füme-added fly ash-based geopolymer mortars. This research can be considered an essential step for further optimizing and popularising geopolymer concrete and microwave curing and proposes a method that should be considered in the future development of more sustainable construction materials.

 Geopolymer concretes a substitute for traditional Portland cement as a more environmentally sustainable alternative. In addition, one of the most significant advantages of geopolymer concrete is the high setting speed that can be achieved with thermal curing, that is, the short curing period. Research on geopolymer concrete has focused on curing, where curing is usually done with conventional ovens. Microwave curing initiates heat generation at the molecular level, which results in a minimal heat increase on the surface of the specimens compared to traditional thermal curing methods. In addition, it provides internal, rapid, and homogeneous heating and rapid strength development. This study is based on research that examined the effect of microwave cure on the compressive strength of silica füme-modified geopolymer mortar. In the study, sodium silicate and sodium hydroxide were used for activation, and first of all, fly ash substituted geopolymer mortar specimens were subjected to conventional thermal curing in an oven. On the other hand, the mortar specimens with the same composition were subjected to short-duration 10 minutes microwave curing at power levels of between 200-600 W. When the results were compared regarding compressive strength, void and percent water absorption, UPV, and SEM-internal structure examination, it was revealed that microwave curing could be used faster than the conventional oven curing method in silica füme-added fly ash-based geopolymer mortars. This research can be considered an essential step for further optimizing and popularising geopolymer concrete and microwave curing and proposes a method that should be considered in the future development of more sustainable construction materials.

Makale detayları

The influence of microwave curing on the strength of silica fume-added fly ash-based geopolymer mortars

Yazarlar:

Berivan Yılmazer Polat

Yayıncı:

Yildiz Technical University

Ana Başlıklar:

Materials Engineering (Other)

Dergi:

Journal of Sustainable Construction Materials and Technologies Vol.8 Issue 3, pp.207-215

Belge Tipi:

Makale

Yayın Tarihi:

3/2023

Belge Dili:

İngilizce

Document ID (Org No.):

2001299824

pISSN:

2458-973X

Microwave curing

fly ash-based geopolymer

early strength

fast cure.

mortar

Sayı

Makale detayları

The influence of microwave curing on the strength of silica fume-added fly ash-based geopolymer mortars

Yazarlar: Berivan Yılmazer Polat

Yayıncı: Yildiz Technical University

Ana Başlıklar: Materials Engineering (Other)

Dergi: Journal of Sustainable Construction Materials and Technologies Vol.8 Issue 3, pp.207-215

Belge Tipi: Makale

Yayın Tarihi: 3/2023

Belge Dili: İngilizce

Document ID (Org No.): 2001299824

pISSN: 2458-973X

Microwave curing

fly ash-based geopolymer

early strength

fast cure.

mortar

Sayı

Yazarlar:

Berivan Yılmazer Polat

Yayıncı:

Yildiz Technical University

Ana Başlıklar:

Materials Engineering (Other)

Dergi:

Journal of Sustainable Construction Materials and Technologies Vol.8 Issue 3, pp.207-215

Belge Tipi:

Makale

Yayın Tarihi:

3/2023

Belge Dili:

İngilizce

Document ID (Org No.):

2001299824

pISSN:

2458-973X