Ultraviolet Protection and Antibacterial Properties of Polylactic Acid Nonwoven Fabrics Coated with Water-Borne Polyurethane/Zinc Oxide Composite Coatings

Gülçin Baysal

Makale detayları

Ultraviolet Protection and Antibacterial Properties of Polylactic Acid Nonwoven Fabrics Coated with Water-Borne Polyurethane/Zinc Oxide Composite Coatings

Yazarlar:

Gülçin Baysal

Yayıncı:

Sakarya University

Ana Başlıklar:

Materials Engineering (Other)

Dergi:

Sakarya University Journal of Science Vol.28 Issue 5, pp.1010-1021

Belge Tipi:

Makale

Yayın Tarihi:

10/2024

Belge Dili:

İngilizce

Document ID (Org No.):

2001329631

pISSN:

2147-835X

Anahtar kelimeler:

Özet:

 This study aimed to create thermally curable, water-borne polyurethanezinc oxide WPUZnO composite coating pastes with varying ZnO concentrations. ZnO nanoparticles were synthesized using a wet chemical process, and the resulting WPUZnO coating pastes were applied to PLA nonwoven fabrics NWFs. In characterization studies, differential scanning calorimetry DSC, scanning electron microscopy SEM, Fourier transform-infrared FTIR spectroscopy, and X-ray diffraction XRD analyses were conducted. Ultraviolet UV protection and antibacterial activity of fabrics were investigated. With WPUZnO composite coatings, the UV protection properties of the coated fabrics were enhanced compared to the uncoated fabric. The highest UPF value of 53.57 was obtained with the fabric coated with the formulation containing a ZnO concentration of 10. This fabric also demonstrated more effective antibacterial activity against both S. aureus and E. coli bacteria. Inhibition zone diameters against E. coli and S. aureus bacteria were measured as 15.5  0.70 mm and 18.25  0.35 mm, respectively. The results of this study illustrate that functional composite coatings for bio-based NWF structures hold great promise for producing effective UV protective and antibacterial materials, potentially setting the stage for future applications.

 This study aimed to create thermally curable, water-borne polyurethanezinc oxide WPUZnO composite coating pastes with varying ZnO concentrations. ZnO nanoparticles were synthesized using a wet chemical process, and the resulting WPUZnO coating pastes were applied to PLA nonwoven fabrics NWFs. In characterization studies, differential scanning calorimetry DSC, scanning electron microscopy SEM, Fourier transform-infrared FTIR spectroscopy, and X-ray diffraction XRD analyses were conducted. Ultraviolet UV protection and antibacterial activity of fabrics were investigated. With WPUZnO composite coatings, the UV protection properties of the coated fabrics were enhanced compared to the uncoated fabric. The highest UPF value of 53.57 was obtained with the fabric coated with the formulation containing a ZnO concentration of 10. This fabric also demonstrated more effective antibacterial activity against both S. aureus and E. coli bacteria. Inhibition zone diameters against E. coli and S. aureus bacteria were measured as 15.5  0.70 mm and 18.25  0.35 mm, respectively. The results of this study illustrate that functional composite coatings for bio-based NWF structures hold great promise for producing effective UV protective and antibacterial materials, potentially setting the stage for future applications.

 This study aimed to create thermally curable, water-borne polyurethanezinc oxide WPUZnO composite coating pastes with varying ZnO concentrations. ZnO nanoparticles were synthesized using a wet chemical process, and the resulting WPUZnO coating pastes were applied to PLA nonwoven fabrics NWFs. In characterization studies, differential scanning calorimetry DSC, scanning electron microscopy SEM, Fourier transform-infrared FTIR spectroscopy, and X-ray diffraction XRD analyses were conducted. Ultraviolet UV protection and antibacterial activity of fabrics were investigated. With WPUZnO composite coatings, the UV protection properties of the coated fabrics were enhanced compared to the uncoated fabric. The highest UPF value of 53.57 was obtained with the fabric coated with the formulation containing a ZnO concentration of 10. This fabric also demonstrated more effective antibacterial activity against both S. aureus and E. coli bacteria. Inhibition zone diameters against E. coli and S. aureus bacteria were measured as 15.5  0.70 mm and 18.25  0.35 mm, respectively. The results of this study illustrate that functional composite coatings for bio-based NWF structures hold great promise for producing effective UV protective and antibacterial materials, potentially setting the stage for future applications.

 This study aimed to create thermally curable, water-borne polyurethanezinc oxide WPUZnO composite coating pastes with varying ZnO concentrations. ZnO nanoparticles were synthesized using a wet chemical process, and the resulting WPUZnO coating pastes were applied to PLA nonwoven fabrics NWFs. In characterization studies, differential scanning calorimetry DSC, scanning electron microscopy SEM, Fourier transform-infrared FTIR spectroscopy, and X-ray diffraction XRD analyses were conducted. Ultraviolet UV protection and antibacterial activity of fabrics were investigated. With WPUZnO composite coatings, the UV protection properties of the coated fabrics were enhanced compared to the uncoated fabric. The highest UPF value of 53.57 was obtained with the fabric coated with the formulation containing a ZnO concentration of 10. This fabric also demonstrated more effective antibacterial activity against both S. aureus and E. coli bacteria. Inhibition zone diameters against E. coli and S. aureus bacteria were measured as 15.5  0.70 mm and 18.25  0.35 mm, respectively. The results of this study illustrate that functional composite coatings for bio-based NWF structures hold great promise for producing effective UV protective and antibacterial materials, potentially setting the stage for future applications.

Makale detayları

Ultraviolet Protection and Antibacterial Properties of Polylactic Acid Nonwoven Fabrics Coated with Water-Borne Polyurethane/Zinc Oxide Composite Coatings

Yazarlar:

Gülçin Baysal

Yayıncı:

Sakarya University

Ana Başlıklar:

Materials Engineering (Other)

Dergi:

Sakarya University Journal of Science Vol.28 Issue 5, pp.1010-1021

Belge Tipi:

Makale

Yayın Tarihi:

10/2024

Belge Dili:

İngilizce

Document ID (Org No.):

2001329631

pISSN:

2147-835X

Zinc oxide

Water-borne polyurethane

Nonwoven fabric

Composite coating

Sayı

Makale detayları

Ultraviolet Protection and Antibacterial Properties of Polylactic Acid Nonwoven Fabrics Coated with Water-Borne Polyurethane/Zinc Oxide Composite Coatings

Yazarlar: Gülçin Baysal

Yayıncı: Sakarya University

Ana Başlıklar: Materials Engineering (Other)

Dergi: Sakarya University Journal of Science Vol.28 Issue 5, pp.1010-1021

Belge Tipi: Makale

Yayın Tarihi: 10/2024

Belge Dili: İngilizce

Document ID (Org No.): 2001329631

pISSN: 2147-835X

Zinc oxide

Water-borne polyurethane

Nonwoven fabric

Composite coating

Sayı

Yazarlar:

Gülçin Baysal

Yayıncı:

Sakarya University

Ana Başlıklar:

Materials Engineering (Other)

Dergi:

Sakarya University Journal of Science Vol.28 Issue 5, pp.1010-1021

Belge Tipi:

Makale

Yayın Tarihi:

10/2024

Belge Dili:

İngilizce

Document ID (Org No.):

2001329631

pISSN:

2147-835X