GLİOKSİLİK ASİDİN İNDİRGEN OLARAK KULLANILDIĞI ELEKTROSUZ BAKIR KAPLANMIŞ POLİESTER KUMAŞLARDA POTASYUM FERROSİYANATIN ETKİSİ

Wenfeng QIN; Ronghui GUO

Makale detayları

GLİOKSİLİK ASİDİN İNDİRGEN OLARAK KULLANILDIĞI ELEKTROSUZ BAKIR KAPLANMIŞ POLİESTER KUMAŞLARDA POTASYUM FERROSİYANATIN ETKİSİ

Yazarlar:

Wenfeng QIN | Ronghui GUO

Yayıncı:

Ege University

Dergi:

Textile and Apparel 2015 Vol.25 Issue 4, pp.319-322

Belge Tipi:

Makale

Yayın Tarihi:

11/2015

Belge Dili:

Türkçe

Document ID (Org No.):

2000651476

Sıklık:

Üç Aylık

eISSN:

2602-3075

pISSN:

1300-3356

Özet:

 

In this study, electroless copper plating on polyester fabric using glyoxylic acid and potassium ferrocyanide (K4Fe (CN) 6) as reducing agent and brightener agent, respectively. Influence of concentration of potassium ferrocyanide (K4Fe (CN) 6) in the plating solution on the deposited rate, morphology and surface resistance of copper plated polyester fabrics were studied. It was found that the deposition rate significantly decreased with the rise of the concentration of K4 Fe (CN)6 and the copper deposits became more compact and smoother. The copper coating on the fabric exhibited a face centered cubic crystal structure. The surface electrical resistance of the obtained copper plated fabric was 13.8 mΩ/sq when 20 mg/L K4Fe(CN)6 was added in the plating solution. The copper plated fabric possesses excellent electrical conductivity.

Makale detayları

GLİOKSİLİK ASİDİN İNDİRGEN OLARAK KULLANILDIĞI ELEKTROSUZ BAKIR KAPLANMIŞ POLİESTER KUMAŞLARDA POTASYUM FERROSİYANATIN ETKİSİ

Yazarlar: Wenfeng QIN | Ronghui GUO

Yayıncı: Ege University

Dergi: Textile and Apparel 2015 Vol.25 Issue 4, pp.319-322

Belge Tipi: Makale

Yayın Tarihi: 11/2015

Belge Dili: Türkçe

Document ID (Org No.): 2000651476

Sıklık: Üç Aylık

eISSN: 2602-3075

pISSN: 1300-3356

Sayı

Yazarlar:

Wenfeng QIN | Ronghui GUO

Yayıncı:

Ege University

Dergi:

Textile and Apparel 2015 Vol.25 Issue 4, pp.319-322

Belge Tipi:

Makale

Yayın Tarihi:

11/2015

Belge Dili:

Türkçe

Document ID (Org No.):

2000651476

Sıklık:

Üç Aylık

eISSN:

2602-3075

pISSN:

1300-3356