Production and Characterization Of Ti-10Cr-3,33Co-3,33Egg Shelter Composite Materials Using By Powder Metallurgy

Ahmet YÖNETKEN; Günnur PESMEN; Ayhan EROL

doi:https://doi.org/10.29137/umagd.474031

Makale detayları

Production and Characterization Of Ti-10Cr-3,33Co-3,33Egg Shelter Composite Materials Using By Powder Metallurgy

Yazarlar:

Ahmet YÖNETKEN | Günnur PESMEN | Ayhan EROL

Yayıncı:

Kirikkale University

Ana Başlıklar:

Uygulamalı fizik

Dergi:

International Journal of Engineering Research and Development 2020 Vol.12 Issue 1, pp.158-165

Belge Tipi:

Makale

Yayın Tarihi:

1/2020

Belge Dili:

İngilizce

Document ID (Org No.):

2000647030

Sıklık:

İki Yıllık

eISSN:

1308-5514

DOI:

https://doi.org/10.29137/umagd.474031

Özet:

 


Titanium-based intermetallic compounds
are frequently used in the production of biomaterials. The behavior of titanium
similar to bone mechanical properties causes the use of titanium as a
biomaterial and preferred among the materials. It also makes its use attractive
in industrial applications at high temperatures. TiCrCo intermetallics are
known to be used together with Ti matrix materials to improve the properties of
the group in addition to elements such as Cr, especially Ti, Co, Mo and Fe in
various application areas. This information is used frequently in the sintering
process. In this study, Ti-10Cr-3,33Co-3,33 egg shelter powders were prepared as a sample mixture. When the properties of the samples produced after sintering are examined, it shows the effects of Co on TiCr. 3.33% Co additive was used in the composition of the composition and mechanical properties were determined in the produced samples. By looking at metallographic analysis, structural features were tried to be determined. The density of the produced samples was calculated, hardness and shear strength were determined. According to the results of the analysis, 3.33% Co composition and 3.71 gr / cm3 density, and 285.5 HV hardness values at 1200 ° C were obtained. In this study,
Ti-10Cr-3,33Co-3,33 egg shelter powders were prepared as a sample mixture. When
the properties of the samples produced after sintering are examined, it shows
the effects of Co on TiCr. 3.33% Co additive was used in the composition of the
composition and mechanical properties were determined in the produced samples.
By looking at metallographic analysis, structural features were tried to be
determined. The density of the produced samples was calculated, hardness and
shear strength were determined. According to the results of the analysis, 3.33%
Co composition and 3.71 gr / cm3 density, and 285.5 HV hardness values at 1200
° C were obtained..

.

Makale detayları

Production and Characterization Of Ti-10Cr-3,33Co-3,33Egg Shelter Composite Materials Using By Powder Metallurgy

Yazarlar: Ahmet YÖNETKEN | Günnur PESMEN | Ayhan EROL

Yayıncı: Kirikkale University

Ana Başlıklar: Uygulamalı fizik

Dergi: International Journal of Engineering Research and Development 2020 Vol.12 Issue 1, pp.158-165

Belge Tipi: Makale

Yayın Tarihi: 1/2020

Belge Dili: İngilizce

Document ID (Org No.): 2000647030

Sıklık: İki Yıllık

eISSN: 1308-5514

DOI: https://doi.org/10.29137/umagd.474031

Sayı

Yazarlar:

Ahmet YÖNETKEN | Günnur PESMEN | Ayhan EROL

Yayıncı:

Kirikkale University

Ana Başlıklar:

Uygulamalı fizik

Dergi:

International Journal of Engineering Research and Development 2020 Vol.12 Issue 1, pp.158-165

Belge Tipi:

Makale

Yayın Tarihi:

1/2020

Belge Dili:

İngilizce

Document ID (Org No.):

2000647030

Sıklık:

İki Yıllık

eISSN:

1308-5514

DOI:

https://doi.org/10.29137/umagd.474031