Effects of Surface Densification Parameters on Hardness, Roughness and Springback of Cylindrical Black Poplar (Populus nigra L.)

Hüseyin Yeşil; Zafer Kaya; Sait Dündar Sofuoğlu

Makale detayları

Effects of Surface Densification Parameters on Hardness, Roughness and Springback of Cylindrical Black Poplar (Populus nigra L.)

Yazarlar:

Hüseyin Yeşil | Zafer Kaya | Sait Dündar Sofuoğlu

Yayıncı:

Kastamonu University

Ana Başlıklar:

Orman Endüstri Mühendisliği (Diğer)

Dergi:

Kastamonu Üniversitesi Orman Fakültesi Dergisi Vol.24 Issue 3, pp.248-259

Belge Tipi:

Makale

Yayın Tarihi:

12/2024

Belge Dili:

İngilizce

Document ID (Org No.):

2001333326

pISSN:

1303-2399

Anahtar kelimeler:

Özet:

 Aim of study: To determine the effect of densification process with heat and steam on hardness, roughness and spring-back in heat-treated and untreated wood to improve the properties of cylindrical wood material Material and method: Turned black poplar Populus nigra L. wood specimens were used in the experiments. The densification process was carried out on an automatic lathe, using a specially designed and produced densification apparatus. During densification, 3 Bar hot steam and 600C dry air were applied to the material. Main results: In general, it has been found that the application of steam and heat in the cylindrical densification process of poplar material has the effect of increasing the roughness and springback values and reducing the surface hardness. It was evaluated that the heat treatment had a positive effect on roughness and springback values. Research highlights: The percentage of spring back and roughness were lower in heat-treated cylindrical black poplar specimens.

 Aim of study: To determine the effect of densification process with heat and steam on hardness, roughness and spring-back in heat-treated and untreated wood to improve the properties of cylindrical wood material Material and method: Turned black poplar Populus nigra L. wood specimens were used in the experiments. The densification process was carried out on an automatic lathe, using a specially designed and produced densification apparatus. During densification, 3 Bar hot steam and 600C dry air were applied to the material. Main results: In general, it has been found that the application of steam and heat in the cylindrical densification process of poplar material has the effect of increasing the roughness and springback values and reducing the surface hardness. It was evaluated that the heat treatment had a positive effect on roughness and springback values. Research highlights: The percentage of spring back and roughness were lower in heat-treated cylindrical black poplar specimens.

 Aim of study: To determine the effect of densification process with heat and steam on hardness, roughness and spring-back in heat-treated and untreated wood to improve the properties of cylindrical wood material Material and method: Turned black poplar Populus nigra L. wood specimens were used in the experiments. The densification process was carried out on an automatic lathe, using a specially designed and produced densification apparatus. During densification, 3 Bar hot steam and 600C dry air were applied to the material. Main results: In general, it has been found that the application of steam and heat in the cylindrical densification process of poplar material has the effect of increasing the roughness and springback values and reducing the surface hardness. It was evaluated that the heat treatment had a positive effect on roughness and springback values. Research highlights: The percentage of spring back and roughness were lower in heat-treated cylindrical black poplar specimens.

 Çalışmanın amacı: Silindirik ağaç malzemenin özelliklerini iyileştirmek için ısıl işlem uygulanmış ve uygulanmamış ahşapta sıcaklık ve buharla birlikte yoğunlaştırma işlemi uygulamasının sertlik, pürüzlülük ve geri esnemeye etkisini belirlemektir. Materyal ve yöntem: Deneylerde tornalanmış karakavak Populus nigra L. odunu örnekler kullanılmıştır. Yoğunlaştırma işlemi özel olarak tasarlanıp imal edilen yoğunlaştırma aparatı kullanılarak otomatik torna tezgahında yapılmıştır. Yoğunlaştırma sırasında malzemeye 3 Bar sıcak buhar ve 600C kuru hava uygulanmıştır. Temel sonuçlar: Genel olarak kavak malzemede silindirik yoğunlaştırma işleminde buhar ve sıcaklık uygulamasının pürüzlülük ve geri esneme değerlerini artırıcı, yüzey sertliğini düşürücü etkisi olduğu tespit edilmiştir. Isıl işlemin pürüzlülük ve geri esneme değerlerinde olumlu etkiye sahip olduğu değerlendirilmiştir. Araştırma vurguları: Isıl işlem görmüş silindirik karakavak numunelerde geri esneme yüzdesi ve pürüzlülük daha düşük elde edilmiştir.

Makale detayları

Effects of Surface Densification Parameters on Hardness, Roughness and Springback of Cylindrical Black Poplar (Populus nigra L.)

Yazarlar:

Hüseyin Yeşil | Zafer Kaya | Sait Dündar Sofuoğlu

Yayıncı:

Kastamonu University

Ana Başlıklar:

Orman Endüstri Mühendisliği (Diğer)

Dergi:

Kastamonu Üniversitesi Orman Fakültesi Dergisi Vol.24 Issue 3, pp.248-259

Belge Tipi:

Makale

Yayın Tarihi:

12/2024

Belge Dili:

İngilizce

Document ID (Org No.):

2001333326

pISSN:

1303-2399

Poplar

Surface Densification

Hardness

Roughness

Spring-back

Heat TreatmentKavak

Yüzey Yoğunlaştırma Sertlik

Pürüzlülük

Geri Esneme

Isıl İşlem

Sayı

Makale detayları

Yazarlar: Hüseyin Yeşil | Zafer Kaya | Sait Dündar Sofuoğlu

Yayıncı: Kastamonu University

Ana Başlıklar: Orman Endüstri Mühendisliği (Diğer)

Dergi: Kastamonu Üniversitesi Orman Fakültesi Dergisi Vol.24 Issue 3, pp.248-259

Belge Tipi: Makale

Yayın Tarihi: 12/2024

Belge Dili: İngilizce

Document ID (Org No.): 2001333326

pISSN: 1303-2399

Sayı

Yazarlar:

Hüseyin Yeşil | Zafer Kaya | Sait Dündar Sofuoğlu

Yayıncı:

Kastamonu University

Ana Başlıklar:

Orman Endüstri Mühendisliği (Diğer)

Dergi:

Kastamonu Üniversitesi Orman Fakültesi Dergisi Vol.24 Issue 3, pp.248-259

Belge Tipi:

Makale

Yayın Tarihi:

12/2024

Belge Dili:

İngilizce

Document ID (Org No.):

2001333326

pISSN:

1303-2399