Effect of shot peening and plasma nitriding processes on wear resistance of AISI 4140 steel

Azmi Erdoğan; Okan Ünal; Mustafa Gök; Soner Özdemir; Sabri Alkan

Makale detayları

Effect of shot peening and plasma nitriding processes on wear resistance of AISI 4140 steel

Yazarlar:

Azmi Erdoğan | Okan Ünal | Mustafa Gök | Soner Özdemir | Sabri Alkan

Yayıncı:

Duzce University

Ana Başlıklar:

Mühendislik

Dergi:

Düzce Üniversitesi Bilim ve Teknoloji Dergisi Vol.12 Issue 2, pp.1126-1135

Belge Tipi:

Makale

Yayın Tarihi:

4/2024

Belge Dili:

Türkçe

Document ID (Org No.):

2001315881

pISSN:

2148-2446

Anahtar kelimeler:

Özet:

 It is aimed to determine how the wear resistance changes by improving the surface properties of AISI 4140 steel, which is frequently used in industrial applications. In this context, AISI 4140 steel was subjected to two different intensities of shot peening and plasma nitration processes. While the changes in the microstructure were determined by SEM and XRD, the change in the surface strength was determined by the microhardness measurement. It was observed that the extra layer formed on the surface as a result of plasma nitriding was iron nitride phases, however, no phase change occurred after the shot peeening processes. All processes increased the surface hardness of the samples and an increase of up to 700 HV was observed on the surface with plasma nitriding. Accordingly, the best wear resistance was achieved by plasma nitriding process. Conventional shot peening had a limited effect on wear resistance, while severe shot peening reduced wear losses considerably. The increase in hardness provided by the applied surface modification processes has been shown to cause the increase in wear resistance. The lack of the expected effect in shot peening is attributed to the roughness on the surface.

 It is aimed to determine how the wear resistance changes by improving the surface properties of AISI 4140 steel, which is frequently used in industrial applications. In this context, AISI 4140 steel was subjected to two different intensities of shot peening and plasma nitration processes. While the changes in the microstructure were determined by SEM and XRD, the change in the surface strength was determined by the microhardness measurement. It was observed that the extra layer formed on the surface as a result of plasma nitriding was iron nitride phases, however, no phase change occurred after the shot peeening processes. All processes increased the surface hardness of the samples and an increase of up to 700 HV was observed on the surface with plasma nitriding. Accordingly, the best wear resistance was achieved by plasma nitriding process. Conventional shot peening had a limited effect on wear resistance, while severe shot peening reduced wear losses considerably. The increase in hardness provided by the applied surface modification processes has been shown to cause the increase in wear resistance. The lack of the expected effect in shot peening is attributed to the roughness on the surface.

 It is aimed to determine how the wear resistance changes by improving the surface properties of AISI 4140 steel, which is frequently used in industrial applications. In this context, AISI 4140 steel was subjected to two different intensities of shot peening and plasma nitration processes. While the changes in the microstructure were determined by SEM and XRD, the change in the surface strength was determined by the microhardness measurement. It was observed that the extra layer formed on the surface as a result of plasma nitriding was iron nitride phases, however, no phase change occurred after the shot peeening processes. All processes increased the surface hardness of the samples and an increase of up to 700 HV was observed on the surface with plasma nitriding. Accordingly, the best wear resistance was achieved by plasma nitriding process. Conventional shot peening had a limited effect on wear resistance, while severe shot peening reduced wear losses considerably. The increase in hardness provided by the applied surface modification processes has been shown to cause the increase in wear resistance. The lack of the expected effect in shot peening is attributed to the roughness on the surface.

 Mevcut çalışmada endüstriyel uygulamalarda sıklıkla kullanılan AISI 4140 çeliğinin yüzey özelliklerinin geliştirilmesi ile aşınma dayanımının nasıl değiştiğinin belirlenmesi amaçlanmıştır. Bu kapsamda AISI 4140 çeliği farklı iki şiddette bilyalı dövme işlemine ve plazma nitrasyon işlemlerine tabi tutulmuştur. Mikroyapıda meydana gelen değişimler SEM ve XRD aracılığıyla belirlenirken yüzey dayanımında meydana gelen değişim mikrosertlik ölçümü ile belirlenmiştir. Plazma nitrürleme sonucunda yüzeyde oluşan ilave katmanın demir nitrür fazları olduğu görülmüş bununla beraber bilyalı dövme işlemlerinden sonra herhangi bir faz değişimi meydana gelmemiştir. Tüm işlemlerle birlikte numunelerin yüzey sertliklerinde artış sağlanmış ve plazma nitrürleme ile yüzeyde 700 HV0.2ye varan sertlik artışı görülmüştür. Buna bağlı olarak en iyi aşınma dayanımı plazma nitrürleme işlemi ile sağlanmıştır. Aşırı bilyalı dövme de aşınma kayıplarının kayda değer miktarda azaltırken geleneksel bilyalı dövme işlemi aşınma dayanımı üzerinde sınırlı bir etki göstermiştir. Uygulanan yüzey modifikasyon işlemlerinin sağladığı sertlik artışı aşınma dayanımında görülen artışa neden olarak gösterilmiştir. Bilyalı dövmede beklenen etkinin görülmemesi ise yüzeyde oluşan pürüzlülüğe atfedilmiştir.

Makale detayları

Effect of shot peening and plasma nitriding processes on wear resistance of AISI 4140 steel

Yazarlar:

Azmi Erdoğan | Okan Ünal | Mustafa Gök | Soner Özdemir | Sabri Alkan

Yayıncı:

Duzce University

Ana Başlıklar:

Mühendislik

Dergi:

Düzce Üniversitesi Bilim ve Teknoloji Dergisi Vol.12 Issue 2, pp.1126-1135

Belge Tipi:

Makale

Yayın Tarihi:

4/2024

Belge Dili:

Türkçe

Document ID (Org No.):

2001315881

pISSN:

2148-2446

AISI 4140

Shot Peening

Plasma NitridingAISI 4140

Bilyalı Dövme

Plazma Nitrürleme

Shot Peening

Plasma Nitriding

Sayı

Makale detayları

Yazarlar: Azmi Erdoğan | Okan Ünal | Mustafa Gök | Soner Özdemir | Sabri Alkan

Yayıncı: Duzce University

Ana Başlıklar: Mühendislik

Dergi: Düzce Üniversitesi Bilim ve Teknoloji Dergisi Vol.12 Issue 2, pp.1126-1135

Belge Tipi: Makale

Yayın Tarihi: 4/2024

Belge Dili: Türkçe

Document ID (Org No.): 2001315881

pISSN: 2148-2446

Sayı

Yazarlar:

Azmi Erdoğan | Okan Ünal | Mustafa Gök | Soner Özdemir | Sabri Alkan

Yayıncı:

Duzce University

Ana Başlıklar:

Mühendislik

Dergi:

Düzce Üniversitesi Bilim ve Teknoloji Dergisi Vol.12 Issue 2, pp.1126-1135

Belge Tipi:

Makale

Yayın Tarihi:

4/2024

Belge Dili:

Türkçe

Document ID (Org No.):

2001315881

pISSN:

2148-2446