The Effects of Different Surface Preparation Techniques on Enamel Surface Properties and Bond Strength

Büşra Akkaya; Yagmur Sener

Makale detayları

The Effects of Different Surface Preparation Techniques on Enamel Surface Properties and Bond Strength

Yazarlar:

Büşra Akkaya | Yagmur Sener

Yayıncı:

Marmara University

Ana Başlıklar:

Paedodontics

Dergi:

European Journal of Research in Dentistry Vol.8 Issue 1, pp.14-25

Belge Tipi:

Makale

Yayın Tarihi:

4/2024

Belge Dili:

İngilizce

Document ID (Org No.):

2001316552

pISSN:

2630-6247

Anahtar kelimeler:

Özet:

 The purpose of this study was to investigate the morphological and chemical changes and bond strength on enamel surfaces subjected to different surface preparation. The samples were evaluated in in vitro tests with 7 different groupsacid etching, Er:YAG laser QSP mode, and Er:YAG laser MSP mode, Air-Flow, and combinations with acid. Surface profilometer and AFM were used to evaluate the surface roughness. After the surface treatment, the chemical changes were analyzed using SEM-EDS. The effects of preparation technique on the bond strength to the enamel surface were evaluated by using micro tensile and shear bond strength tests. The values obtained the surface roughness evaluation of surface profilometer and AFM were compatible with each other. The highest roughness value was found in QSP when all groups were compared. CaP ratios of the surfaces were evaluated as a result of SEM-EDS analysis and it was observed that CaP ratio increased in all groups except Acid. It was seen that the results obtained for all groups of micro tensile and shear bond strength tests were consistent with each other. In conclusion, it is considered the use of Er:YAG laser QSP settings with acid can effect the long-term success of restorations clinically.

 The purpose of this study was to investigate the morphological and chemical changes and bond strength on enamel surfaces subjected to different surface preparation. The samples were evaluated in in vitro tests with 7 different groupsacid etching, Er:YAG laser QSP mode, and Er:YAG laser MSP mode, Air-Flow, and combinations with acid. Surface profilometer and AFM were used to evaluate the surface roughness. After the surface treatment, the chemical changes were analyzed using SEM-EDS. The effects of preparation technique on the bond strength to the enamel surface were evaluated by using micro tensile and shear bond strength tests. The values obtained the surface roughness evaluation of surface profilometer and AFM were compatible with each other. The highest roughness value was found in QSP when all groups were compared. CaP ratios of the surfaces were evaluated as a result of SEM-EDS analysis and it was observed that CaP ratio increased in all groups except Acid. It was seen that the results obtained for all groups of micro tensile and shear bond strength tests were consistent with each other. In conclusion, it is considered the use of Er:YAG laser QSP settings with acid can effect the long-term success of restorations clinically.

 The purpose of this study was to investigate the morphological and chemical changes and bond strength on enamel surfaces subjected to different surface preparation. The samples were evaluated in in vitro tests with 7 different groupsacid etching, Er:YAG laser QSP mode, and Er:YAG laser MSP mode, Air-Flow, and combinations with acid. Surface profilometer and AFM were used to evaluate the surface roughness. After the surface treatment, the chemical changes were analyzed using SEM-EDS. The effects of preparation technique on the bond strength to the enamel surface were evaluated by using micro tensile and shear bond strength tests. The values obtained the surface roughness evaluation of surface profilometer and AFM were compatible with each other. The highest roughness value was found in QSP when all groups were compared. CaP ratios of the surfaces were evaluated as a result of SEM-EDS analysis and it was observed that CaP ratio increased in all groups except Acid. It was seen that the results obtained for all groups of micro tensile and shear bond strength tests were consistent with each other. In conclusion, it is considered the use of Er:YAG laser QSP settings with acid can effect the long-term success of restorations clinically.

 Bu çalışmanın amacı, farklı yüzey hazırlığına tabi tutulan mine yüzeylerdeki morfolojik ve kimyasal değişimler ile bağlanma mukavemetinin araştırılmasıdır. Örnekler in vitro testlerde kullanılmak üzere 7 farklı gruba asit dağlama, Er:YAG lazer QSP modu ve Er:YAG lazer MSP modu, Air-Flow ve asitle kombinasyonlar ayrıldı. Yüzey pürüzlülüğünü değerlendirmek için yüzey profilometresi ve AFM kullanıldı. Yüzey işleminden sonra kimyasal değişiklikler SEM-EDS kullanılarak analiz edildi. Preparasyon tekniğinin mine yüzeyine bağlanma dayanımı üzerindeki etkileri mikro gerilim ve makaslama bağlanma dayanımı testleri kullanılarak değerlendirildi. Yüzey profilometresi ve AFMnin yüzey pürüzlülüğü değerlendirmesinden elde edilen değerler birbiriyle uyumluydu. Tüm gruplar karşılaştırıldığında en yüksek pürüzlülük değeri QSPde bulundu. SEM-EDS analizi sonucunda yüzeylerin CaP oranları değerlendirilmiş ve Asit dışındaki tüm gruplarda CaP oranının arttığı görülmüştür. Mikro gerilim ve makaslama bağlanma dayanımı testlerinde tüm gruplar için elde edilen sonuçların birbiriyle uyumlu olduğu görüldü. Sonuç olarak, Er:YAG lazer QSP ayarlarının asitle birlikte kullanılmasının klinik olarak restorasyonların uzun vadeli başarısını etkileyebileceği düşünülmektedir.

Makale detayları

The Effects of Different Surface Preparation Techniques on Enamel Surface Properties and Bond Strength

Yazarlar:

Büşra Akkaya | Yagmur Sener

Yayıncı:

Marmara University

Ana Başlıklar:

Paedodontics

Dergi:

European Journal of Research in Dentistry Vol.8 Issue 1, pp.14-25

Belge Tipi:

Makale

Yayın Tarihi:

4/2024

Belge Dili:

İngilizce

Document ID (Org No.):

2001316552

pISSN:

2630-6247

AFM

Enamel

SEM-EDS

Surface PreparationAFM

Mine

SEM-EDS

Yüzey Hazırlığı

Sayı

Makale detayları

Yazarlar: Büşra Akkaya | Yagmur Sener

Yayıncı: Marmara University

Ana Başlıklar: Paedodontics

Dergi: European Journal of Research in Dentistry Vol.8 Issue 1, pp.14-25

Belge Tipi: Makale

Yayın Tarihi: 4/2024

Belge Dili: İngilizce

Document ID (Org No.): 2001316552

pISSN: 2630-6247

Sayı

Yazarlar:

Büşra Akkaya | Yagmur Sener

Yayıncı:

Marmara University

Ana Başlıklar:

Paedodontics

Dergi:

European Journal of Research in Dentistry Vol.8 Issue 1, pp.14-25

Belge Tipi:

Makale

Yayın Tarihi:

4/2024

Belge Dili:

İngilizce

Document ID (Org No.):

2001316552

pISSN:

2630-6247