Effect of ASTM D638 Specimen Type on the Tensile Properties of Fused Deposition Modelling 3D-Printed PLA Specimens

Roaa Gomaa; Sara Eltahir; Cagatay Yilmaz

Makale detayları

Effect of ASTM D638 Specimen Type on the Tensile Properties of Fused Deposition Modelling 3D-Printed PLA Specimens

Yazarlar:

Roaa Gomaa | Sara Eltahir | Cagatay Yilmaz

Yayıncı:

Erciyes University

Ana Başlıklar:

Malzeme Karekterizasyonu

Dergi:

Erciyes Üniversitesi Fen Bilimleri Enstitüsü Fen Bilimleri Dergisi Vol.41 Issue 2, pp.412-431

Belge Tipi:

Makale

Yayın Tarihi:

8/2025

Belge Dili:

İngilizce

Document ID (Org No.):

2001354049

pISSN:

1012-2354

Anahtar kelimeler:

Özet:

 This research examines how different ASTM-D638 specimen types affect the mechanical properties of 3D-printed PLA materials. Specimen types refer to specific configurations of test samples used in mechanical testing, as defined by ASTM-D638 standards, which include five different types: Type I  Type V. This standard outline various specimen geometries and dimensions to ensure consistent and comparable testing procedures for Polylactic acid PLA related studies. Computer-aided design CAD models are created and Fused Deposition Modeling FDM 3D printing is used to produce PLA specimens. Tensile testing and Digital Image Correlation DIC analysis are performed to measure the strength and strain of the samples, respectively. The study aims to provide comprehensive data on specimen types impact on part properties and demonstrate a cost-effective strain measurement method using DIC and a smartphone. The methodology includes CAD modeling, 3D printing, surface preparation, tensile testing, DIC analysis using Ncorr, and MATLAB data processing. Results show stress-strain curves and average strain values, with Type I and Type II exhibiting the highest ultimate tensile strength UTS of 43.179 MPa and 43.164 MPa, respectively. However, Type V is the most optimum option due to its short printing time and low filament usage which are 5 times less than Type I, and a reasonable UTS of 42.640 MPa. This research fills a knowledge gap on specimen designs influence on 3D-printed part properties, providing valuable insights for future research.

 This research examines how different ASTM-D638 specimen types affect the mechanical properties of 3D-printed PLA materials. Specimen types refer to specific configurations of test samples used in mechanical testing, as defined by ASTM-D638 standards, which include five different types: Type I  Type V. This standard outline various specimen geometries and dimensions to ensure consistent and comparable testing procedures for Polylactic acid PLA related studies. Computer-aided design CAD models are created and Fused Deposition Modeling FDM 3D printing is used to produce PLA specimens. Tensile testing and Digital Image Correlation DIC analysis are performed to measure the strength and strain of the samples, respectively. The study aims to provide comprehensive data on specimen types impact on part properties and demonstrate a cost-effective strain measurement method using DIC and a smartphone. The methodology includes CAD modeling, 3D printing, surface preparation, tensile testing, DIC analysis using Ncorr, and MATLAB data processing. Results show stress-strain curves and average strain values, with Type I and Type II exhibiting the highest ultimate tensile strength UTS of 43.179 MPa and 43.164 MPa, respectively. However, Type V is the most optimum option due to its short printing time and low filament usage which are 5 times less than Type I, and a reasonable UTS of 42.640 MPa. This research fills a knowledge gap on specimen designs influence on 3D-printed part properties, providing valuable insights for future research.

 This research examines how different ASTM-D638 specimen types affect the mechanical properties of 3D-printed PLA materials. Specimen types refer to specific configurations of test samples used in mechanical testing, as defined by ASTM-D638 standards, which include five different types: Type I  Type V. This standard outline various specimen geometries and dimensions to ensure consistent and comparable testing procedures for Polylactic acid PLA related studies. Computer-aided design CAD models are created and Fused Deposition Modeling FDM 3D printing is used to produce PLA specimens. Tensile testing and Digital Image Correlation DIC analysis are performed to measure the strength and strain of the samples, respectively. The study aims to provide comprehensive data on specimen types impact on part properties and demonstrate a cost-effective strain measurement method using DIC and a smartphone. The methodology includes CAD modeling, 3D printing, surface preparation, tensile testing, DIC analysis using Ncorr, and MATLAB data processing. Results show stress-strain curves and average strain values, with Type I and Type II exhibiting the highest ultimate tensile strength UTS of 43.179 MPa and 43.164 MPa, respectively. However, Type V is the most optimum option due to its short printing time and low filament usage which are 5 times less than Type I, and a reasonable UTS of 42.640 MPa. This research fills a knowledge gap on specimen designs influence on 3D-printed part properties, providing valuable insights for future research.

 Bu araştırma, farklı ASTM-D638 numune türlerinin 3D baskılı PLA malzemelerinin mekanik özelliklerini nasıl etkilediğini incelemektedir. Numune türleri, ASTM-D638 standartlarında tanımlandığı gibi, beş farklı türü içeren, mekanik testlerde kullanılan test numunelerinin belirli konfigürasyonlarını ifade eder: Tip I  Tip V. Bu standart, tutarlı ve karşılaştırılabilir test prosedürlerini sağlamak için çeşitli numune geometrilerini ve boyutlarını özetlemektedir. Polilaktik asit PLA ile ilgili çalışmalar. Bilgisayar destekli tasarım CAD modelleri oluşturulur ve PLA numuneleri üretmek için Erimiş Biriktirme Modelleme FDM 3D baskı kullanılır. Numunelerin mukavemetini ve gerinimini ölçmek için sırasıyla çekme testi ve Dijital Görüntü Korelasyonu DIC analizi yapılır. Çalışma, numune türünün parça özellikleri üzerindeki etkisine ilişkin kapsamlı veriler sağlamayı ve DIC ve akıllı telefon kullanılarak uygun maliyetli bir gerinim ölçüm yöntemi göstermeyi amaçlıyor. Metodoloji, CAD modellemeyi, 3D yazdırmayı, yüzey hazırlığını, çekme testini, Ncorr kullanılarak DIC analizini ve MATLAB veri işlemeyi içerir. Sonuçlar, Tip I ve Tip IInin sırasıyla 43,179 MPa ve 43,164 MPa ile en yüksek nihai gerilme mukavemetini UTS sergilediği gerilim-gerinim eğrilerini ve ortalama gerinim değerlerini gösterir. Ancak Tip V, kısa baskı süresi ve Tip Ie göre 5 kat daha az olan düşük filament kullanımı ve 42.640 MPalık makul UTSsi nedeniyle en optimum seçenektir. Bu araştırma, numune tasarımının 3D baskılı parça özellikleri üzerindeki etkisine ilişkin bilgi boşluğunu doldurarak gelecekteki araştırmalar için değerli bilgiler sağlıyor.

Makale detayları

Effect of ASTM D638 Specimen Type on the Tensile Properties of Fused Deposition Modelling 3D-Printed PLA Specimens

Yazarlar:

Roaa Gomaa | Sara Eltahir | Cagatay Yilmaz

Yayıncı:

Erciyes University

Ana Başlıklar:

Malzeme Karekterizasyonu

Dergi:

Erciyes Üniversitesi Fen Bilimleri Enstitüsü Fen Bilimleri Dergisi Vol.41 Issue 2, pp.412-431

Belge Tipi:

Makale

Yayın Tarihi:

8/2025

Belge Dili:

İngilizce

Document ID (Org No.):

2001354049

pISSN:

1012-2354

Fused Deposition Modeling (FDM)

Polylactic Acid (PLA)

Digital Image Correlation (DIC)

Tensile TestingEriyik Yığma Modellemesi

Poli Laktik Asit (PLA)

Sayısal Görüntü Korelasyonu

Çekme Testi

Sayı

Makale detayları

Yazarlar: Roaa Gomaa | Sara Eltahir | Cagatay Yilmaz

Yayıncı: Erciyes University

Ana Başlıklar: Malzeme Karekterizasyonu

Dergi: Erciyes Üniversitesi Fen Bilimleri Enstitüsü Fen Bilimleri Dergisi Vol.41 Issue 2, pp.412-431

Belge Tipi: Makale

Yayın Tarihi: 8/2025

Belge Dili: İngilizce

Document ID (Org No.): 2001354049

pISSN: 1012-2354

Sayı

Yazarlar:

Roaa Gomaa | Sara Eltahir | Cagatay Yilmaz

Yayıncı:

Erciyes University

Ana Başlıklar:

Malzeme Karekterizasyonu

Dergi:

Erciyes Üniversitesi Fen Bilimleri Enstitüsü Fen Bilimleri Dergisi Vol.41 Issue 2, pp.412-431

Belge Tipi:

Makale

Yayın Tarihi:

8/2025

Belge Dili:

İngilizce

Document ID (Org No.):

2001354049

pISSN:

1012-2354