The influence of process parameters on the formation of Al coating on steel by planetary ball-milling

Fatih ERDEMİR

Makale detayları

The influence of process parameters on the formation of Al coating on steel by planetary ball-milling

Yazarlar:

Fatih ERDEMİR

Yayıncı:

Eskisehir Technical University

Dergi:

Eskişehir Technical University Journal of Science and Technology A - Applied Sciences and Engineering 2018 Vol.19 Issue 3, pp.748-755

Belge Tipi:

Makale

Yayın Tarihi:

8/2018

Belge Dili:

Türkçe

Document ID (Org No.):

2000417050

pISSN:

2667-4211

Özet:

 

The effect of milling time, ball/powder ratio, and milling speed of planetary ball-mıllıng process on coating thickness was investigated by central composite design. The interaction effects of the factors were determined through Analysis of Variance (ANOVA). The regression model was developed for evaluatıng the coating thickness.  A Scanning Electron Microscopy (SEM) was used for measurıng the coating thickness. The results show that the ball/powder ratio was the most significant factor to maximize the coating thickness. The maximum coating thickness of 164 µm  was succeed at a milling speed of 400 rpm, ball-to-powder ratio of 15:1 and  milling time of 8 h. Although minimum coating thickness of 7 µm was attained at a milling speed of 200 rpm and ball/powder ratio of 5:1.

Makale detayları

The influence of process parameters on the formation of Al coating on steel by planetary ball-milling

Yazarlar: Fatih ERDEMİR

Yayıncı: Eskisehir Technical University

Dergi: Eskişehir Technical University Journal of Science and Technology A - Applied Sciences and Engineering 2018 Vol.19 Issue 3, pp.748-755

Belge Tipi: Makale

Yayın Tarihi: 8/2018

Belge Dili: Türkçe

Document ID (Org No.): 2000417050

pISSN: 2667-4211

Sayı

Yazarlar:

Fatih ERDEMİR

Yayıncı:

Eskisehir Technical University

Dergi:

Eskişehir Technical University Journal of Science and Technology A - Applied Sciences and Engineering 2018 Vol.19 Issue 3, pp.748-755

Belge Tipi:

Makale

Yayın Tarihi:

8/2018

Belge Dili:

Türkçe

Document ID (Org No.):

2000417050

pISSN:

2667-4211