THE EVALUATION OF BOND STRENGTH BETWEEN DENTAL CERAMIC AND BASE METAL ALLOYS FABRICATED BY CASTING AND LASER SINTERING

Yurdanur UÇAR; Elif Figen KOÇAK; Orhun EKREN

Makale detayları

THE EVALUATION OF BOND STRENGTH BETWEEN DENTAL CERAMIC AND BASE METAL ALLOYS FABRICATED BY CASTING AND LASER SINTERING

Yazarlar:

Yurdanur UÇAR | Elif Figen KOÇAK | Orhun EKREN

Yayıncı:

Ataturk University

Ana Başlıklar:

Cerrahi ve ilgili tıbbi uzmanlıklar

Dergi:

Atatürk Üniversitesi Diş Hekimliği Fakültesi Dergisi 2019 Vol.29 Issue 3, pp.455-460

Belge Tipi:

Makale

Yayın Tarihi:

7/2019

Belge Dili:

İngilizce

Document ID (Org No.):

2000892058

Sıklık:

Üç Aylık

eISSN:

2822-2555

Anahtar kelimeler:

Özet:

 




Amaç: Bu
çalışmanın amacı lazer sinterize
Co-Cr ve döküm yöntemi ile elde edilen Ni-Cr ve Co-Cr alaşımlarının porselen
ile bağlantısını 3-nokta-bükme testi (3-Point-Bending; 3PB) kullanarak
değerlendirmektir. 

Gereç-Yöntem: Çalışmada metal altyapı olarak 3 farklı grup kullanılmıştır: lazer
sinterize Co-Cr, döküm Co-Cr ve döküm Ni-Cr. Her grup için 15 örnek ISO
9693(1999) standartlarına uygun olarak hazırlanmış ve 3PB testi kullanılarak
bağlanma dayanımı değerlendirilmiştir. Veriler ANOVA ve  sonrasında Tukey çok yönlü karşılaştırma testi
kullanılarak değerlendirilmiştir (α=0,05). 

Bulgular: Bükülme modülü
ve ortalama en yüksek bükme dayanımı değerleri karşılaştırıldığında her iki
parametre için 3 grup arasında istatistiksel fark bulunmuştur (P=0,0001). En
düşük ortalama bükülme modülü lazer sinterize grupta gözlenirken (77±6,5 GPa),
en yüksek değer döküm Co-Cr grubunda (247±16 GPa) görülmüştür. İkili karşılaştırmalarda
her 3 grup da birbirinden farklı bulunmuştur. Ortalama bükülme dayanımı
değerleri karşılaştırıldığında ise en yüksek dayanım değeri lazer sinterize
Co-Cr (87±9 MPa) grubunda bulunurken, döküm Co-Cr grubunun bükülme dayanımı (78±13
MPa) daha düşük olmakla birlikte aradaki farkın istatistiksel açıdan anlamlı
olmadığı görülmüştür (P=0,094). Ancak döküm Ni-Cr grubunun ortalama bükülme
dayanımı değeri (45±11 MPa) Co-Cr gruplarından anlamlı şekilde daha düşük
bulunmuştur (P=0,0001).

Sonuç: Bu çalışmanın
sınırları dâhilinde lazer sinterize Co-Cr altyapılarının porselen ile güçlü bir
bağlantı oluşturduğu sonucuna varılmıştır.

Anahtar
kelimeler: Hızlı Üretim, CAD/CAM, Lazer Sinterleme, Döküm, Bağlanma Dayanımı



THE EVALUATION OF BOND
STRENGTH BETWEEN DENTAL CERAMIC AND BASE METAL ALLOYS FABRICATED BY CASTING AND
LASER SINTERING

Abstract

Aim: The aim
of this study was to evaluate bond strength of laser sintered Co-Cr and cast
Co-Cr and Ni-Cr alloys to porcelain using 3-point-bending test (3PB test). 

Material and Methods: 3 different metal frameworks were used in the current study: laser
sintered Co-Cr, cast Co-Cr and cast Ni-Cr. Fifteen specimens per group were
prepared according to ISO 9693 standard (1999) and tested using 3PB test.
Results were analyzed using one-way ANOVA followed by Tukey multiple comparison
test (α=0,05). 

Results: Mean
bending modulus and flexural bending strength were statistically significantly
different among 3 groups (P=0,0001). The lowest mean bending modulus was observed
for laser sintered Co-Cr group (77±6,5 GPa) and the highest value was observed
for cast Co-Cr group (247±16 GPa). Pairwise comparisons have shown
statistically significant differences between all compared groups. When mean
bending strength values were compared, the highest value was observed for laser
sintered Co-Cr group (87±9 MPa). Although mean flexural strength value of cast
Co-Cr group (78±13 MPa) was lower than the laser sintered one, the difference
was not statistically significant (P=0,094). However, the mean bending strength
of cast Ni-Cr (45±11 MPa) was significantly lower than the Co-Cr groups (P=0,0001).


Conclusion: Within the limitations of this study, it can be concluded that laser
sintered Co-Cr frameworks establish a strong bond with porcelain.   

Key Words: Rapid manufacturing, CAD/CAM, Laser
Sintering, Casting, Bond Strength   

.

Makale detayları

THE EVALUATION OF BOND STRENGTH BETWEEN DENTAL CERAMIC AND BASE METAL ALLOYS FABRICATED BY CASTING AND LASER SINTERING

Yazarlar: Yurdanur UÇAR | Elif Figen KOÇAK | Orhun EKREN

Yayıncı: Ataturk University

Ana Başlıklar: Cerrahi ve ilgili tıbbi uzmanlıklar

Dergi: Atatürk Üniversitesi Diş Hekimliği Fakültesi Dergisi 2019 Vol.29 Issue 3, pp.455-460

Belge Tipi: Makale

Yayın Tarihi: 7/2019

Belge Dili: İngilizce

Document ID (Org No.): 2000892058

Sıklık: Üç Aylık

eISSN: 2822-2555

Hızlı Üretim

CAD/CAM

Lazer Sinterleme

Döküm

Sayı

Yazarlar:

Yurdanur UÇAR | Elif Figen KOÇAK | Orhun EKREN

Yayıncı:

Ataturk University

Ana Başlıklar:

Cerrahi ve ilgili tıbbi uzmanlıklar

Dergi:

Atatürk Üniversitesi Diş Hekimliği Fakültesi Dergisi 2019 Vol.29 Issue 3, pp.455-460

Belge Tipi:

Makale

Yayın Tarihi:

7/2019

Belge Dili:

İngilizce

Document ID (Org No.):

2000892058

Sıklık:

Üç Aylık

eISSN:

2822-2555