Effect of Commercial Whitening Toothpastes on Color Stability and Surface Roughness of Two Different Composite Resins

N.A.

Makale detayları

Effect of Commercial Whitening Toothpastes on Color Stability and Surface Roughness of Two Different Composite Resins

Yazarlar:

N.A.

Yayıncı:

Ataturk University

Ana Başlıklar:

Restoratif Diş Tedavisi

Dergi:

Current Research in Dental Sciences Vol.34 Issue 1, pp.9-17

Belge Tipi:

Makale

Yayın Tarihi:

1/2024

Belge Dili:

İngilizce

Document ID (Org No.):

2001311350

pISSN:

2822-2555

Anahtar kelimeler:

Özet:

 ABSTRACT Objective: The aim of this in vitro study is to compare the effects of different whitening tooth- pastes on the color stability CS and surface roughness SR of 2 composite resins. Methods: A hundred disc-shaped specimens were prepared from Filtek Z250 microhybrid and Charisma Topaz nanohybrid composite resins. The discs were divided into 5 subgroups: artificial saliva, Colgate Active Charcoal, Yotuel, Opalescence, and Sensodyne Promine toothpastes. The initial roughness and color values of the samples were measured. In order to evaluate the CS and SR, all specimens were subjected to coffee and brushing cycles. A three-way mixed analysis of variance was used to analyze the data. All analyses were performed considering α  0.05. Results: While the Z250 composite showed higher E values than the other composite P  .05, no significant differences were observed between the composites regarding SR P  .05. Among the whitening toothpaste groups, there were no significant differences in E values P  .05 except for the control group. After an 8-week cycle, the activated carbon- containing toothpaste group showed a higher SR than the control group P  .05. Conclusion: All toothpastes were effective in removing discoloration from composite res- ins, depending on the composite resin used. However, the whitening toothpastes tested after 8 weeks of use increased surface roughness regardless of the composite resins used, but not more than regular toothpaste not containing a whitening ingredient. Keywords: Composite resins, discoloration, surface roughness, toothpastes ÖZ Amaç: Bu in vitro çalışmanın amacı, farklı beyazlatıcı diş macunlarının iki kompozit reçinenin renk stabilitesi CS ve yüzey pürüzlülüğü SR üzerindeki etkilerini karşılaştırmaktır. Yöntemler: Filtek Z250 mikrohibrit ve Charisma Topaz nanohibrit kompozit reçinelerinden yüz adet disk şeklinde örnek hazırlandı. Diskler beş alt gruba ayrıldı: yapay tükürük, Colgate Aktif Karbon, Yotuel, Opalescence ve Sensodyne Promine diş macunları. Örneklerin başlangıç pürüz- lülük ve renk değerleri ölçüldü. CS ve SRyi değerlendirmek için tüm örnekler kahve ve fırçalama döngülerine tabi tutuldu. Verilerin analizi için üç yönlü karma varyans analizi kullanıldı. Tüm analiz- ler α  0.05 düzeyinde yapıldı. Bulgular: Z250 kompoziti, diğer kompozite göre daha yüksek E değerleri gösterirken P  .05, kompozitler arasında SR açısından anlamlı bir fark gözlenmedi P  .05. Beyazlatıcı diş macunu grupları arasında, kontrol grubu hariç E değerlerinde anlamlı bir fark bulunmadı P  .05. Sekiz haftalık döngü sonrasında, aktif karbon içeren diş macunu grubu, kontrol grubuna göre daha yük- sek SR gösterdi P  .05. Sonuç: Tüm diş macunları, kullanılan kompozit reçineye bağlı olarak kompozit reçinelerden renk- lenmeyi gidermede etkiliydi. Test edilen beyazlatıcı diş macunları sekiz haftalık kullanım sonrası kullanılan kompozit reçinelere bakılmaksızın, ancak beyazlatıcı etkili olmayan diş macunundan daha fazla olmayacak şekilde yüzey pürüzlülüğünü artırdı. Anahtar Kelimeler: Kompozit reçineler, renk değişimi, yüzey pürüzlülüğü, diş macunları.

 ABSTRACT Objective: The aim of this in vitro study is to compare the effects of different whitening tooth- pastes on the color stability CS and surface roughness SR of 2 composite resins. Methods: A hundred disc-shaped specimens were prepared from Filtek Z250 microhybrid and Charisma Topaz nanohybrid composite resins. The discs were divided into 5 subgroups: artificial saliva, Colgate Active Charcoal, Yotuel, Opalescence, and Sensodyne Promine toothpastes. The initial roughness and color values of the samples were measured. In order to evaluate the CS and SR, all specimens were subjected to coffee and brushing cycles. A three-way mixed analysis of variance was used to analyze the data. All analyses were performed considering α  0.05. Results: While the Z250 composite showed higher E values than the other composite P  .05, no significant differences were observed between the composites regarding SR P  .05. Among the whitening toothpaste groups, there were no significant differences in E values P  .05 except for the control group. After an 8-week cycle, the activated carbon- containing toothpaste group showed a higher SR than the control group P  .05. Conclusion: All toothpastes were effective in removing discoloration from composite res- ins, depending on the composite resin used. However, the whitening toothpastes tested after 8 weeks of use increased surface roughness regardless of the composite resins used, but not more than regular toothpaste not containing a whitening ingredient. Keywords: Composite resins, discoloration, surface roughness, toothpastes ÖZ Amaç: Bu in vitro çalışmanın amacı, farklı beyazlatıcı diş macunlarının iki kompozit reçinenin renk stabilitesi CS ve yüzey pürüzlülüğü SR üzerindeki etkilerini karşılaştırmaktır. Yöntemler: Filtek Z250 mikrohibrit ve Charisma Topaz nanohibrit kompozit reçinelerinden yüz adet disk şeklinde örnek hazırlandı. Diskler beş alt gruba ayrıldı: yapay tükürük, Colgate Aktif Karbon, Yotuel, Opalescence ve Sensodyne Promine diş macunları. Örneklerin başlangıç pürüz- lülük ve renk değerleri ölçüldü. CS ve SRyi değerlendirmek için tüm örnekler kahve ve fırçalama döngülerine tabi tutuldu. Verilerin analizi için üç yönlü karma varyans analizi kullanıldı. Tüm analiz- ler α  0.05 düzeyinde yapıldı. Bulgular: Z250 kompoziti, diğer kompozite göre daha yüksek E değerleri gösterirken P  .05, kompozitler arasında SR açısından anlamlı bir fark gözlenmedi P  .05. Beyazlatıcı diş macunu grupları arasında, kontrol grubu hariç E değerlerinde anlamlı bir fark bulunmadı P  .05. Sekiz haftalık döngü sonrasında, aktif karbon içeren diş macunu grubu, kontrol grubuna göre daha yük- sek SR gösterdi P  .05. Sonuç: Tüm diş macunları, kullanılan kompozit reçineye bağlı olarak kompozit reçinelerden renk- lenmeyi gidermede etkiliydi. Test edilen beyazlatıcı diş macunları sekiz haftalık kullanım sonrası kullanılan kompozit reçinelere bakılmaksızın, ancak beyazlatıcı etkili olmayan diş macunundan daha fazla olmayacak şekilde yüzey pürüzlülüğünü artırdı. Anahtar Kelimeler: Kompozit reçineler, renk değişimi, yüzey pürüzlülüğü, diş macunları.

 ABSTRACT Objective: The aim of this in vitro study is to compare the effects of different whitening tooth- pastes on the color stability CS and surface roughness SR of 2 composite resins. Methods: A hundred disc-shaped specimens were prepared from Filtek Z250 microhybrid and Charisma Topaz nanohybrid composite resins. The discs were divided into 5 subgroups: artificial saliva, Colgate Active Charcoal, Yotuel, Opalescence, and Sensodyne Promine toothpastes. The initial roughness and color values of the samples were measured. In order to evaluate the CS and SR, all specimens were subjected to coffee and brushing cycles. A three-way mixed analysis of variance was used to analyze the data. All analyses were performed considering α  0.05. Results: While the Z250 composite showed higher E values than the other composite P  .05, no significant differences were observed between the composites regarding SR P  .05. Among the whitening toothpaste groups, there were no significant differences in E values P  .05 except for the control group. After an 8-week cycle, the activated carbon- containing toothpaste group showed a higher SR than the control group P  .05. Conclusion: All toothpastes were effective in removing discoloration from composite res- ins, depending on the composite resin used. However, the whitening toothpastes tested after 8 weeks of use increased surface roughness regardless of the composite resins used, but not more than regular toothpaste not containing a whitening ingredient. Keywords: Composite resins, discoloration, surface roughness, toothpastes ÖZ Amaç: Bu in vitro çalışmanın amacı, farklı beyazlatıcı diş macunlarının iki kompozit reçinenin renk stabilitesi CS ve yüzey pürüzlülüğü SR üzerindeki etkilerini karşılaştırmaktır. Yöntemler: Filtek Z250 mikrohibrit ve Charisma Topaz nanohibrit kompozit reçinelerinden yüz adet disk şeklinde örnek hazırlandı. Diskler beş alt gruba ayrıldı: yapay tükürük, Colgate Aktif Karbon, Yotuel, Opalescence ve Sensodyne Promine diş macunları. Örneklerin başlangıç pürüz- lülük ve renk değerleri ölçüldü. CS ve SRyi değerlendirmek için tüm örnekler kahve ve fırçalama döngülerine tabi tutuldu. Verilerin analizi için üç yönlü karma varyans analizi kullanıldı. Tüm analiz- ler α  0.05 düzeyinde yapıldı. Bulgular: Z250 kompoziti, diğer kompozite göre daha yüksek E değerleri gösterirken P  .05, kompozitler arasında SR açısından anlamlı bir fark gözlenmedi P  .05. Beyazlatıcı diş macunu grupları arasında, kontrol grubu hariç E değerlerinde anlamlı bir fark bulunmadı P  .05. Sekiz haftalık döngü sonrasında, aktif karbon içeren diş macunu grubu, kontrol grubuna göre daha yük- sek SR gösterdi P  .05. Sonuç: Tüm diş macunları, kullanılan kompozit reçineye bağlı olarak kompozit reçinelerden renk- lenmeyi gidermede etkiliydi. Test edilen beyazlatıcı diş macunları sekiz haftalık kullanım sonrası kullanılan kompozit reçinelere bakılmaksızın, ancak beyazlatıcı etkili olmayan diş macunundan daha fazla olmayacak şekilde yüzey pürüzlülüğünü artırdı. Anahtar Kelimeler: Kompozit reçineler, renk değişimi, yüzey pürüzlülüğü, diş macunları.

 ABSTRACT Objective: The aim of this in vitro study is to compare the effects of different whitening tooth- pastes on the color stability CS and surface roughness SR of 2 composite resins. Methods: A hundred disc-shaped specimens were prepared from Filtek Z250 microhybrid and Charisma Topaz nanohybrid composite resins. The discs were divided into 5 subgroups: artificial saliva, Colgate Active Charcoal, Yotuel, Opalescence, and Sensodyne Promine toothpastes. The initial roughness and color values of the samples were measured. In order to evaluate the CS and SR, all specimens were subjected to coffee and brushing cycles. A three-way mixed analysis of variance was used to analyze the data. All analyses were performed considering α  0.05. Results: While the Z250 composite showed higher E values than the other composite P  .05, no significant differences were observed between the composites regarding SR P  .05. Among the whitening toothpaste groups, there were no significant differences in E values P  .05 except for the control group. After an 8-week cycle, the activated carbon- containing toothpaste group showed a higher SR than the control group P  .05. Conclusion: All toothpastes were effective in removing discoloration from composite res- ins, depending on the composite resin used. However, the whitening toothpastes tested after 8 weeks of use increased surface roughness regardless of the composite resins used, but not more than regular toothpaste not containing a whitening ingredient. Keywords: Composite resins, discoloration, surface roughness, toothpastes ÖZ Amaç: Bu in vitro çalışmanın amacı, farklı beyazlatıcı diş macunlarının iki kompozit reçinenin renk stabilitesi CS ve yüzey pürüzlülüğü SR üzerindeki etkilerini karşılaştırmaktır. Yöntemler: Filtek Z250 mikrohibrit ve Charisma Topaz nanohibrit kompozit reçinelerinden yüz adet disk şeklinde örnek hazırlandı. Diskler beş alt gruba ayrıldı: yapay tükürük, Colgate Aktif Karbon, Yotuel, Opalescence ve Sensodyne Promine diş macunları. Örneklerin başlangıç pürüz- lülük ve renk değerleri ölçüldü. CS ve SRyi değerlendirmek için tüm örnekler kahve ve fırçalama döngülerine tabi tutuldu. Verilerin analizi için üç yönlü karma varyans analizi kullanıldı. Tüm analiz- ler α  0.05 düzeyinde yapıldı. Bulgular: Z250 kompoziti, diğer kompozite göre daha yüksek E değerleri gösterirken P  .05, kompozitler arasında SR açısından anlamlı bir fark gözlenmedi P  .05. Beyazlatıcı diş macunu grupları arasında, kontrol grubu hariç E değerlerinde anlamlı bir fark bulunmadı P  .05. Sekiz haftalık döngü sonrasında, aktif karbon içeren diş macunu grubu, kontrol grubuna göre daha yük- sek SR gösterdi P  .05. Sonuç: Tüm diş macunları, kullanılan kompozit reçineye bağlı olarak kompozit reçinelerden renk- lenmeyi gidermede etkiliydi. Test edilen beyazlatıcı diş macunları sekiz haftalık kullanım sonrası kullanılan kompozit reçinelere bakılmaksızın, ancak beyazlatıcı etkili olmayan diş macunundan daha fazla olmayacak şekilde yüzey pürüzlülüğünü artırdı. Anahtar Kelimeler: Kompozit reçineler, renk değişimi, yüzey pürüzlülüğü, diş macunları.

Makale detayları

Effect of Commercial Whitening Toothpastes on Color Stability and Surface Roughness of Two Different Composite Resins

Yazarlar: N.A.

Yayıncı: Ataturk University

Ana Başlıklar: Restoratif Diş Tedavisi

Dergi: Current Research in Dental Sciences Vol.34 Issue 1, pp.9-17

Belge Tipi: Makale

Yayın Tarihi: 1/2024

Belge Dili: İngilizce

Document ID (Org No.): 2001311350

pISSN: 2822-2555

Composite resins

discoloration

surface roughness

toothpastes

Sayı

Yazarlar:

N.A.

Yayıncı:

Ataturk University

Ana Başlıklar:

Restoratif Diş Tedavisi

Dergi:

Current Research in Dental Sciences Vol.34 Issue 1, pp.9-17

Belge Tipi:

Makale

Yayın Tarihi:

1/2024

Belge Dili:

İngilizce

Document ID (Org No.):

2001311350

pISSN:

2822-2555