Investigation of the effects of hot dip aluminizing and diffusion annealing on microstructural and tribological properties of dual phase (DP800) steels

Yakup Yürektürk

Makale detayları

Investigation of the effects of hot dip aluminizing and diffusion annealing on microstructural and tribological properties of dual phase (DP800) steels

Yazarlar:

Yakup Yürektürk

Yayıncı:

Pamukkale University

Ana Başlıklar:

Makine Mühendisliği (Diğer)

Dergi:

Pamukkale Üniversitesi Mühendislik Bilimleri Dergisi Vol.30 Issue 6, pp.737-741

Belge Tipi:

Makale

Yayın Tarihi:

11/2024

Belge Dili:

İngilizce

Document ID (Org No.):

2001332007

pISSN:

2147-5881

Anahtar kelimeler:

Özet:

 In this study, the effects of hot dip aluminizing HDA 90 s at 725C and diffusion annealing on the microstructural and tribological properties of DP800 steel were investigated. After HDA treatment, one of the sample was left to cool in air HDA-1 and the other one left to cool in air after being subjected to a diffusion annealing for 1 hour in an oven set at 300C HDA-2. Evolution in mechanical and tribological properties depending on the developments in the coating microstructure investigated in terms of hardness and wear behaviour, respectively. Mechanical characterization results show that diffusion annealing increases the hardness value of hot dip aluminized steel to 1100 HV values. Considering the wear ball volume and friction coefficients, the most advanced tribological properties were observed in the diffusion-annealed HDA process HDA-2.

 In this study, the effects of hot dip aluminizing HDA 90 s at 725C and diffusion annealing on the microstructural and tribological properties of DP800 steel were investigated. After HDA treatment, one of the sample was left to cool in air HDA-1 and the other one left to cool in air after being subjected to a diffusion annealing for 1 hour in an oven set at 300C HDA-2. Evolution in mechanical and tribological properties depending on the developments in the coating microstructure investigated in terms of hardness and wear behaviour, respectively. Mechanical characterization results show that diffusion annealing increases the hardness value of hot dip aluminized steel to 1100 HV values. Considering the wear ball volume and friction coefficients, the most advanced tribological properties were observed in the diffusion-annealed HDA process HDA-2.

 In this study, the effects of hot dip aluminizing HDA 90 s at 725C and diffusion annealing on the microstructural and tribological properties of DP800 steel were investigated. After HDA treatment, one of the sample was left to cool in air HDA-1 and the other one left to cool in air after being subjected to a diffusion annealing for 1 hour in an oven set at 300C HDA-2. Evolution in mechanical and tribological properties depending on the developments in the coating microstructure investigated in terms of hardness and wear behaviour, respectively. Mechanical characterization results show that diffusion annealing increases the hardness value of hot dip aluminized steel to 1100 HV values. Considering the wear ball volume and friction coefficients, the most advanced tribological properties were observed in the diffusion-annealed HDA process HDA-2.

 Bu çalışmada, sıcak daldırmalı alüminyumlama HDA 725Cde 90 sn. ve difüzyon tavlaması işleminin DP800 çeliğinin mikroyapısal ve tribolojik özellikleri üzerindeki etkileri incelenmiştir. HDA işleminden sonra numunelerden biri havada HDA-1, diğeri ise 300Cye ayarlanmış fırında HDA-2 1 saat difüzyon tavlaması işlemine tabi tutularak havada soğumaya bırakılmıştır. Kaplama mikroyapısındaki dönüşüme bağlı olarak değişen mekanik ve tribolojik özellikler sırasıyla sertlik ve aşınma davranışı bakımından incelenmiştir. Mekanik karakterizasyon sonuçları, difüzyon tavlaması işleminin sıcak daldırma alüminize çeliğin sertlik değerini 1100 HV değerlerine çıkardığını göstermektedir. Aşınan bilye hacmi ve sürtünme katsayıları dikkate alındığında en gelişmiş tribolojik özellikler difüzyon tavlaması işlemi görmüş HDA prosesinde HDA-2 gözlenmiştir.

Makale detayları

Investigation of the effects of hot dip aluminizing and diffusion annealing on microstructural and tribological properties of dual phase (DP800) steels

Yazarlar:

Yakup Yürektürk

Yayıncı:

Pamukkale University

Ana Başlıklar:

Makine Mühendisliği (Diğer)

Dergi:

Pamukkale Üniversitesi Mühendislik Bilimleri Dergisi Vol.30 Issue 6, pp.737-741

Belge Tipi:

Makale

Yayın Tarihi:

11/2024

Belge Dili:

İngilizce

Document ID (Org No.):

2001332007

pISSN:

2147-5881

DP800 steel

Hot dip aluminizing

Diffusion annealing

WearDP800 çelik

Sıcak daldırma alüminyumlama

Difüzyon tavlaması

Aşınma

Sayı

Makale detayları

Yazarlar: Yakup Yürektürk

Yayıncı: Pamukkale University

Ana Başlıklar: Makine Mühendisliği (Diğer)

Dergi: Pamukkale Üniversitesi Mühendislik Bilimleri Dergisi Vol.30 Issue 6, pp.737-741

Belge Tipi: Makale

Yayın Tarihi: 11/2024

Belge Dili: İngilizce

Document ID (Org No.): 2001332007

pISSN: 2147-5881

Sayı

Yazarlar:

Yakup Yürektürk

Yayıncı:

Pamukkale University

Ana Başlıklar:

Makine Mühendisliği (Diğer)

Dergi:

Pamukkale Üniversitesi Mühendislik Bilimleri Dergisi Vol.30 Issue 6, pp.737-741

Belge Tipi:

Makale

Yayın Tarihi:

11/2024

Belge Dili:

İngilizce

Document ID (Org No.):

2001332007

pISSN:

2147-5881