KIYMETSİZ ALAŞIMLARA UYGULANAN KİMYASAL DAĞLAMA (ETCHING) İŞLEMİNİN DEĞİŞİK SÜRELERDEKİ ETKİSİNİN SEM'DE İNCELENMESİ (BÖLÜM I)-SEM ANALYSIS OF CHROMIUM-NICKEL AND CHROMIUM-COBALT ALLOY SURFACES DIFFIRENT ETCHING TIMES (PART I)

Yasemin ARAS; Sevtap GÜRSU

Makale detayları

KIYMETSİZ ALAŞIMLARA UYGULANAN KİMYASAL DAĞLAMA (ETCHING) İŞLEMİNİN DEĞİŞİK SÜRELERDEKİ ETKİSİNİN SEM'DE İNCELENMESİ (BÖLÜM I)-SEM ANALYSIS OF CHROMIUM-NICKEL AND CHROMIUM-COBALT ALLOY SURFACES DIFFIRENT ETCHING TIMES (PART I)

Yazarlar:

Yasemin ARAS | Sevtap GÜRSU

Yayıncı:

Istanbul University

Dergi:

Journal of Istanbul University Faculty of Dentistry 1992 Vol.26 Issue 2, pp.59-63

Belge Tipi:

Makale

Yayın Tarihi:

6/2013

Belge Dili:

Türkçe

Document ID (Org No.):

2000427531

eISSN:

2651-2823

pISSN:

2630-6158

Özet:

 


ÖZET

Cr-Ni ve Cr-Co melal alaşımlarından dökülerek hazırlanan 120 adet metal disk'in (5 mm. çapında, 1 mm. kalınlığında) 24 adedi kontrol grubu olarak her iki bolümde kullanılmak üzere ayrıldı. 96 adedine değişik sürelerde (15, 30, 45, 60 dakika) kimyasal etehing işlemi uygulandı. Ullraso-nik sistemde temizlenip kurutulduktan sonra metal alaşımlarının yüzeyleri SEM'de incelenerek fotoğrafları alındı.

Sonuçta, en kısa sürede mikrorctansiyonlar Cr-Ni alaşımında görüldü.

Anahtar sözcükler: Melal alaşımları, tutuculuk, dağlama.

ABSTRACT

Chemical etching procedure was applied on metal discs casled with Chromium-Nickel and Chromium-Cobalt alloys in different etching limes. The etched metal surfaces were then examined with the SEM at x6(K) magnification.

Cr-Ni alloy samples has shown an efficient micro-retention by chemical etching in shortest time intervals.

Key words: Metal alloys, retention, etching.

 

.

Makale detayları

KIYMETSİZ ALAŞIMLARA UYGULANAN KİMYASAL DAĞLAMA (ETCHING) İŞLEMİNİN DEĞİŞİK SÜRELERDEKİ ETKİSİNİN SEM'DE İNCELENMESİ (BÖLÜM I)-SEM ANALYSIS OF CHROMIUM-NICKEL AND CHROMIUM-COBALT ALLOY SURFACES DIFFIRENT ETCHING TIMES (PART I)

Yazarlar: Yasemin ARAS | Sevtap GÜRSU

Yayıncı: Istanbul University

Dergi: Journal of Istanbul University Faculty of Dentistry 1992 Vol.26 Issue 2, pp.59-63

Belge Tipi: Makale

Yayın Tarihi: 6/2013

Belge Dili: Türkçe

Document ID (Org No.): 2000427531

eISSN: 2651-2823

pISSN: 2630-6158

Sayı

Yazarlar:

Yasemin ARAS | Sevtap GÜRSU

Yayıncı:

Istanbul University

Dergi:

Journal of Istanbul University Faculty of Dentistry 1992 Vol.26 Issue 2, pp.59-63

Belge Tipi:

Makale

Yayın Tarihi:

6/2013

Belge Dili:

Türkçe

Document ID (Org No.):

2000427531

eISSN:

2651-2823

pISSN:

2630-6158