Investigation of Corrosion Behaviours Hydroxyapatite (HAP) coated Ti6Al4V Implants by Using Electrochemical Deposition Method

Aysel Büyüksağiş; Yusuf Kayalı

Makale detayları

Investigation of Corrosion Behaviours Hydroxyapatite (HAP) coated Ti6Al4V Implants by Using Electrochemical Deposition Method

Yazarlar:

Aysel Büyüksağiş | Yusuf Kayalı

Yayıncı:

Afyon Kocatepe University

Dergi:

Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi 2018 Vol.18 Issue 3, pp.807-819

Belge Tipi:

Makale

Yayın Tarihi:

12/2018

Belge Dili:

İngilizce

Document ID (Org No.):

2000845616

Sıklık:

İki Aylık

eISSN:

2149-3367

Anahtar kelimeler:

Özet:

 

In this research, hydroxyapatite (HAP) has been coated on the Ti6A14V alloy surface by electrophoresis method. In this electrophoresis method, NH4H2PO4 is taken as P precursor and Ca (NO3)2.4H2O is taken as Ca precursor to obtain HAP coating. Additionally, 5 N NaOH pre-treatment surface operation (PTSO) has been applied to Ti6A14V. PTSO are effective on clinging of HAP coating to the surface. The corrosion behaviours of uncoated and HAP coated samples are examined in simulated body fluid (SBF) after for holded 7, 14, 21 and 35 days in SBF. HAP coatings have obtained by electrophoresis method was not showed inhibition for preventing corrosion. The surface images of the samples were described by scanning electron microscope (SEM), energy dispersive X-ray analysis (EDX), and X-ray diffraction (XRD). From SEM images have been observed open pores and connections among pores in the coating, which increases osteointegration. It is noted in EDX analyses of the surfaces of the HAP coated samples that there is Ca, O and P on the surface. It is seen in XRD analysis of HAP coated samples that there are TiO2, HAP and calcium phosphate structures on the surfaces.

Makale detayları

Investigation of Corrosion Behaviours Hydroxyapatite (HAP) coated Ti6Al4V Implants by Using Electrochemical Deposition Method

Yazarlar:

Aysel Büyüksağiş | Yusuf Kayalı

Yayıncı:

Afyon Kocatepe University

Dergi:

Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi 2018 Vol.18 Issue 3, pp.807-819

Belge Tipi:

Makale

Yayın Tarihi:

12/2018

Belge Dili:

İngilizce

Document ID (Org No.):

2000845616

Sıklık:

İki Aylık

eISSN:

2149-3367

Electrophoresis

Hydroxyapatite

Corrosion

Ti6Al4V.

Sayı

Makale detayları

Investigation of Corrosion Behaviours Hydroxyapatite (HAP) coated Ti6Al4V Implants by Using Electrochemical Deposition Method

Yazarlar: Aysel Büyüksağiş | Yusuf Kayalı

Yayıncı: Afyon Kocatepe University

Dergi: Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi 2018 Vol.18 Issue 3, pp.807-819

Belge Tipi: Makale

Yayın Tarihi: 12/2018

Belge Dili: İngilizce

Document ID (Org No.): 2000845616

Sıklık: İki Aylık

eISSN: 2149-3367

Electrophoresis

Hydroxyapatite

Corrosion

Ti6Al4V.

Sayı

Yazarlar:

Aysel Büyüksağiş | Yusuf Kayalı

Yayıncı:

Afyon Kocatepe University

Dergi:

Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi 2018 Vol.18 Issue 3, pp.807-819

Belge Tipi:

Makale

Yayın Tarihi:

12/2018

Belge Dili:

İngilizce

Document ID (Org No.):

2000845616

Sıklık:

İki Aylık

eISSN:

2149-3367