Experimental analysis of laminated particleboard case-type furniture reinforced by polymer composite layer

Nurdan Çetin Yerlikaya -

Makale detayları

Experimental analysis of laminated particleboard case-type furniture reinforced by polymer composite layer

Yazarlar:

Nurdan Çetin Yerlikaya -

Yayıncı:

Usak University

Dergi:

Usak University Journal of Material Sciences 2013 Vol.2 Issue 1, pp.7-22

Belge Tipi:

Makale

Yayın Tarihi:

5/2013

Belge Dili:

Türkçe

Document ID (Org No.):

2000841437

Sıklık:

İki Yıllık

pISSN:

2147-2785

Anahtar kelimeler:

Özet:

 

In this study, the effects of reinforced corner joints by polymer composite layer in case-type furniture have been analyzed experimentally and statistically in laminated particleboard material. The failure loads of corner joints have been analyzed experimentally under compression and tension moments. These joint types are dowel (D), dowel+fabric from the outside (DCO), dowel+fabric from the inside (DCI), dowel+fabric from the outside and inside (DCOI), and dowel+fabric from the edge (DCE). The test results were analyzed statistically by Weibull distribution. Results show that the failure load takes its highest value in the DCOI case both for the test results and for 95% reliability under Weibull distribution. On the other hand, it takes its lowest value in the D case. Reinforced corner joints are more strength than unreinforced corner joints. In addition, the 95% reliability value for each corner joint configuration is approximately equivalent to the 0.52 value of the failure load.

 

In this study, the effects of reinforced corner joints by polymer composite layer in case-type furniture have been analyzed experimentally and statistically in laminated particleboard material. The failure loads of corner joints have been analyzed experimentally under compression and tension moments. These joint types are dowel (D), dowel+fabric from the outside (DCO), dowel+fabric from the inside (DCI), dowel+fabric from the outside and inside (DCOI), and dowel+fabric from the edge (DCE). The test results were analyzed statistically by Weibull distribution. Results show that the failure load takes its highest value in the DCOI case both for the test results and for 95% reliability under Weibull distribution. On the other hand, it takes its lowest value in the D case. Reinforced corner joints are more strength than unreinforced corner joints. In addition, the 95% reliability value for each corner joint configuration is approximately equivalent to the 0.52 value of the failure load.

Makale detayları

Experimental analysis of laminated particleboard case-type furniture reinforced by polymer composite layer

Yazarlar:

Nurdan Çetin Yerlikaya -

Yayıncı:

Usak University

Dergi:

Usak University Journal of Material Sciences 2013 Vol.2 Issue 1, pp.7-22

Belge Tipi:

Makale

Yayın Tarihi:

5/2013

Belge Dili:

Türkçe

Document ID (Org No.):

2000841437

Sıklık:

İki Yıllık

pISSN:

2147-2785

Composites

fabrics

reinforced

failure analysis

case-type furniture

corner joint

Sayı

Makale detayları

Experimental analysis of laminated particleboard case-type furniture reinforced by polymer composite layer

Yazarlar: Nurdan Çetin Yerlikaya -

Yayıncı: Usak University

Dergi: Usak University Journal of Material Sciences 2013 Vol.2 Issue 1, pp.7-22

Belge Tipi: Makale

Yayın Tarihi: 5/2013

Belge Dili: Türkçe

Document ID (Org No.): 2000841437

Sıklık: İki Yıllık

pISSN: 2147-2785

Composites

fabrics

reinforced

failure analysis

case-type furniture

corner joint

Sayı

Yazarlar:

Nurdan Çetin Yerlikaya -

Yayıncı:

Usak University

Dergi:

Usak University Journal of Material Sciences 2013 Vol.2 Issue 1, pp.7-22

Belge Tipi:

Makale

Yayın Tarihi:

5/2013

Belge Dili:

Türkçe

Document ID (Org No.):

2000841437

Sıklık:

İki Yıllık

pISSN:

2147-2785